POM TARNOFORM® TARNOFORM200 GRUPA AZOTY POLAND
116
- Unit Price:
- $2435 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 39MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | Saturation，23℃ | ISO 62 | 0.8 | % |
| Equilibrium，23℃，50% RH | ISO 62 | 0.2 | % | |
| Melt volume flow rate | 190℃，2.16 kg | ISO 1133 | 2.2 | cm3/10min |
| Shrinkage rate | MD：2.0 mm | ISO 294-4 | 2 | % |
| Melt mass flow rate | 190℃，2.16kg 1 | ISO 1133 | 2.5 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending strength | ISO 178 | 60 | Mpa | |
| Ball pressure hardness | H358/30 | ISO 2039-1 | 140 | Mpa |
| Tensile modulus | ISO 527-1-2 | 2600 | Mpa | |
| tensile strength | Yield | ISO 527-2/50 | 60 | Mpa |
| Bending modulus | ISO 178 | 2400 | Mpa | |
| Tensile strain | Yield Yield | ISO 527-2/50 | 14 | % |
| Break Break | ISO 527-2/50 | 50 | % |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Type ISO Type | ISO 1874 | POM-K, M-GNR, 01-02 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | 100000000000000 | ohms | |
| Volume resistivity | IEC 60093 | 1000000000000000 | ohms·cm | |
| Dielectric strength | 2 mm 2.00 mm | IEC 60243-1 | 25 | KV/mm |
| Compared to the leakage trace index | Solution A | IEC 60112 | 600 | V |
| Dielectric constant | 1 Hz 1 Hz | IEC 60250 | 3.8 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -- -- | ISO 179/1eU | 无断裂 | |
| -30°C | ISO 179/1eU | 200 | kJ/m² | |
| Impact strength of cantilever beam gap | ISO 180 | 8 | kJ/m² |
| Flame retardant performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame retardant grade 3.2 mm | 3.20 mm | UL 94 | HB | |
| Burning rate | FMVSS 302 | < 100 | mm/min |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD：23~55℃ | ISO 11359-2 | 0.00011 | 1/℃ |
| Vicat softening temperature | ISO 306/B | 150 | °C | |
| Hot deformation temperature | 1.8 MPa，Unannealed | ISO 75-2/A | 105 | °C |
| Melting temperature | ISO 11357-3 | 167 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.