Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM TARNOFORM200 GRUPA AZOTY POLAND
TARNOFORM®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
POM/GRUPA AZOTY POLAND/TARNOFORM200
Density
ISO 1183
g/cm³
1
Melt volume flow rate
190℃，2.16 kg
ISO 1133
cm3/10min
2
Melt mass flow rate
190℃，2.16kg 1
ISO 1133
g/10min
2
Shrinkage rate
MD：2.0 mm
ISO 294-4
%
2
Water absorption rate
饱和，23℃
ISO 62
%
0
Water absorption rate
平衡，23℃，50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
POM/GRUPA AZOTY POLAND/TARNOFORM200
Tensile modulus
ISO 527-1-2
Mpa
2
tensile strength
屈服
ISO 527-2/50
Mpa
6
Tensile strain
屈服 Yield
ISO 527-2/50
%
1
Tensile strain
断裂 Break
ISO 527-2/50
%
5
Ball pressure hardness
H358/30
ISO 2039-1
Mpa
1
Bending modulus
ISO 178
Mpa
2
Bending strength
ISO 178
Mpa
6
Impact performance
Test Condition
Test Method
Unit
POM/GRUPA AZOTY POLAND/TARNOFORM200
Impact strength of simply supported beam without notch
-30°C
ISO 179/1eU
kJ/m²
2
Impact strength of cantilever beam gap
ISO 180
kJ/m²
8
Thermal performance
Test Condition
Test Method
Unit
POM/GRUPA AZOTY POLAND/TARNOFORM200
Hot deformation temperature
1.8 MPa，未退火
ISO 75-2/A
°C
1
Melting temperature
ISO 11357-3
°C
1
Vicat softening temperature
ISO 306/B
°C
1
Linear coefficient of thermal expansion
MD：23~55℃
ISO 11359-2
1/℃
0
Flame retardant performance
Test Condition
Test Method
Unit
POM/GRUPA AZOTY POLAND/TARNOFORM200
Burning rate
FMVSS 302
mm/min
<
Electrical performance
Test Condition
Test Method
Unit
POM/GRUPA AZOTY POLAND/TARNOFORM200
Surface resistivity
IEC 60093
ohms
1
Dielectric strength
2 mm 2.00 mm
IEC 60243-1
KV/mm
2
Volume resistivity
IEC 60093
ohms·cm
1
Compared to the leakage trace index
解决方案 A
IEC 60112
V
6