POM TENAC™ FS410 ASAHI JAPAN
130
- Unit Price:
- $5315 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 60MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High sliding wear resistant
- Application Areas:bearing
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.42 | ||
| Molding shrinkage rate | ASTM D955 | 1.8-2.2 | % | |
| Melt index (flow coefficient) | ASTM D1238/ISO 1133 | 9 | g/10min | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 0.2 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | ASTM D570 | 0.2 | % | |
| Shrinkage rate | -，Flow | 旭化成法 | 1.8-2.2 | % |
| -，Across Flow | 旭化成法 | 1.8-2.2 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | ASTM D638/ISO 527 | 67 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 94 | ||
| Bending modulus | ASTM D790/ISO 178 | 2940 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 98 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638 | 67 | Mpa | |
| Elongation rate | ASTM D638 | 30 | % | |
| bending strength | ASTM D790 | 98 | Mpa | |
| Bending modulus | ASTM D790 | 2940 | Mpa | |
| IZOD notch impact strength | ASTM D256 | 39 | J/m | |
| Rockwell hardness | ASTM D785 | 94 | M | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 30 | % | |
| IZOD notch impact strength | ASTM D256/ISO 179 | 39 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flame retardancy | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 170 | ℃（℉） | |
| ASTM D648/ISO 75 | 136 | ℃（℉） | ||
| Melt index | ASTM D1238 | 9 | g/10min | |
| Coefficient of linear expansion | TMA法 | 10 | ||
| Hot deformation temperature | -，1.82MPa | ASTM D648 | 136 | °C |
| -，0.45MPa | ASTM D648 | 170 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.