Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM FS410 ASAHI JAPAN
TENAC™
bearing
High sliding、wear resistant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
POM/ASAHI JAPAN/FS410
Molding shrinkage rate
ASTM D955
%
1
Melt index (flow coefficient)
ASTM D1238/ISO 1133
g/10min
9
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
0
physical property
Test Condition
Test Method
Unit
POM/ASAHI JAPAN/FS410
Shrinkage rate
-，平行方向
旭化成法
%
1
Shrinkage rate
-，垂直方向
旭化成法
%
1
Water absorption rate
ASTM D570
%
0
Mechanical performance
Test Condition
Test Method
Unit
POM/ASAHI JAPAN/FS410
IZOD notch impact strength
ASTM D256
J/m
3
tensile strength
ASTM D638
Mpa
6
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
6
Rockwell hardness
ASTM D785
M
9
Bending modulus
ASTM D790
Mpa
2
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
9
bending strength
ASTM D790
Mpa
9
Elongation rate
ASTM D638
%
3
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
3
Tensile elongation at break (elongation at break)
ASTM D638/ISO 527
%
3
Thermal performance
Test Condition
Test Method
Unit
POM/ASAHI JAPAN/FS410
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
1
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
1
Hot deformation temperature
-，1.82MPa
ASTM D648
°C
1
Hot deformation temperature
-，0.45MPa
ASTM D648
°C
1
Melt index
ASTM D1238
g/10min
9