HDPE UNIVL™ DMDD-6200 DOW JAPAN
115
- Unit Price:
- $1236 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 0.25 | g/10min |
| 190°C/21.6kg | ASTMD1238 | 23 | g/10min | |
| Resistance to environmental stress cracking | 50°C,100%Igepal,F50 | ASTMD1693 | 50.0 | hr |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Yield | ASTMD638 | 26.2 | Mpa |
| Break | ASTMD638 | 25.5 | Mpa | |
| elongation | Yield | ASTMD638 | 6.0 | % |
| Break | ASTMD638 | 900 | % | |
| Bending modulus -2% secant | ASTMD790B | 1020 | Mpa | |
| Environmental cracking stress | 50℃，10% Igepal，F50 | ASTM D-1693 | 50 | hr |
| Tensile yield strength | ASTM D-638 | 26.2 | Mpa | |
| Tensile fracture strength | ASTM D-638 | 25.5 | Mpa | |
| Tensile yield elongation | ASTM D-638 | 6 | % | |
| Tensile strain at break | ASTM D-638 | 900 | % | |
| Bending modulus -2% Secant | ASTM D-790B | 1020 | Mpa | |
| Tensile impact strength | ASTM D-1822 | 210 | KJ/m | |
| Shore hardness | Shore D | ASTM D-2240 | 59 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa，Unannealed | ASTM D-648 | 70 | °C |
| Brittle temperature | ASTM D-746 | °C | ||
| vicat softening point | ASTM D-1525 | 129 | °C | |
| Melting temperature | Internal Method | 132 | °C | |
| Peak crystallization temperature | Internal Method | 119 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 70.0 | °C |
| Brittle temperature | ASTMD746 | <-76.1 | °C | |
| Vicat softening temperature | ASTMD1525 | 129 | °C | |
| Melting temperature (DSC) | 内部方法 | 132 | °C | |
| Crystallization peak temperature | DSC | 内部方法 | 119 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile impact strength 3 | ASTMD1822 | 210 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | Shore D | ASTMD2240 | 59 |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D-792 | 0.953 | g/cm | |
| Melt index | 190℃/2.16kg | ASTM D-1238 | 0.25 | g/10min |
| 190℃/21.6kg | ASTM D-1238 | 23 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.