HDPE DMDD-6200 DOW JAPAN
UNIVL™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
HDPE/DOW JAPAN/DMDD-6200
Resistance to environmental stress cracking
50°C,100%Igepal,F50
ASTMD1693
hr
5
Melt mass flow rate
190°C/2.16kg
ASTMD1238
g/10min
0
Melt mass flow rate
190°C/21.6kg
ASTMD1238
g/10min
2
Mechanical performance
Test Condition
Test Method
Unit
HDPE/DOW JAPAN/DMDD-6200
Environmental cracking stress
50℃，10% Igepal，F50
ASTM D-1693
hr
5
Tensile impact strength
ASTM D-1822
KJ/m
2
Tensile strength
屈服
ASTMD638
Mpa
2
Tensile strength
断裂
ASTMD638
Mpa
2
Tensile fracture strength
ASTM D-638
Mpa
2
Tensile strain at break
ASTM D-638
%
9
Tensile yield strength
ASTM D-638
Mpa
2
Tensile yield elongation
ASTM D-638
%
6
elongation
屈服
ASTMD638
%
6
elongation
断裂
ASTMD638
%
9
Bending modulus -2% Secant
ASTM D-790B
Mpa
1
Bending modulus -2% secant
ASTMD790B
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
HDPE/DOW JAPAN/DMDD-6200
Brittle temperature
ASTMD746
°C
<
Brittle temperature
ASTM D-746
°C
Peak crystallization temperature
Internal Method
°C
1
Crystallization peak temperature
DSC
内部方法
°C
1
Hot deformation temperature
0.45MPa,未退火
ASTMD648
°C
7
Hot deformation temperature
0.45MPa，Unannealed
ASTM D-648
°C
7
Melting temperature (DSC)
内部方法
°C
1
Melting temperature
Internal Method
°C
1
vicat softening point
ASTM D-1525
°C
1
Vicat softening temperature
ASTMD1525
°C
1
Impact performance
Test Condition
Test Method
Unit
HDPE/DOW JAPAN/DMDD-6200
Tensile impact strength 3
ASTMD1822
kJ/m²
2
Basic performance
Test Condition
Test Method
Unit
HDPE/DOW JAPAN/DMDD-6200
density
ASTM D-792
g/cm
0
Melt index
190℃/2.16kg
ASTM D-1238
g/10min
0
Melt index
190℃/21.6kg
ASTM D-1238
g/10min
2