PA6 Ultramid® 8200HS BK102 BASF GERMANY

130

Unit Price:
$3168 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
70MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Thermal stability high strength Oil resistant
Application Areas:Gear Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD：3.18mm		1.2	%
Water absorption rate	24hr	ASTMD570	1.6	%
	Water absorption rate	23°C,24hr	ISO62	1.6	%
		Water absorption rate	Saturation	ASTMD570	9.5	%
			Water absorption rate	Saturation,23°C	ISO62	9.5	%
				Water absorption rate	Equilibrium,23°C,50%RH	ISO62	2.7	%
				Water absorption rate	Water absorption rate	Equilibrium,50%RH	ASTMD570	2.7	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	23°C	ISO527-2	2700	Mpa
elongation	Yield,-40°C	ASTMD638	3.0	%
	elongation	Yield,23°C	ASTMD638	20	%
		elongation	Break,-40°C	ASTMD638	8.0	%
			elongation	Break,23°C	ASTMD638	60	%
				elongation	Break,121°C	ASTMD638	>100	%
				elongation	elongation	Yield,121°C	ASTMD638	15	%
Bending modulus	-40°C	ASTMD790	3010	Mpa
	Bending modulus	23°C	ASTMD790	2830	Mpa
		Bending modulus	65°C	ASTMD790	460	Mpa
			Bending modulus	90°C	ASTMD790	350	Mpa
				Bending modulus	121°C	ASTMD790	305	Mpa
				Bending modulus	Bending modulus	23°C	ISO178	2400	Mpa
bending strength	-40°C	ASTMD790	168	Mpa
	bending strength	23°C	ASTMD790	110	Mpa
		bending strength	65°C	ASTMD790	30.0	Mpa
			bending strength	90°C	ASTMD790	20.0	Mpa
			bending strength	bending strength	121°C	ASTMD790	18.0	Mpa
Tensile stress	Yield,-40°C	ISO527-2	136	Mpa
	Tensile stress	Yield,23°C	ISO527-2	80.0	Mpa
	Tensile stress	Tensile stress	Yield,120°C	ISO527-2	23.0	Mpa
Tensile strain	Yield,23°C	ISO527-2	5.0	%
Tensile strength	Yield,-40°C	ASTMD638	136	Mpa
	Tensile strength	Yield,23°C	ASTMD638	85.0	Mpa
	Tensile strength	Tensile strength	Yield,121°C	ASTMD638	23.0	Mpa
Bending stress	23°C	ISO178	82.0	Mpa
Nominal tensile fracture strain	-40°C	ISO527-2	8.0	%
	Nominal tensile fracture strain	23°C	ISO527-2	25	%
	Nominal tensile fracture strain	Nominal tensile fracture strain	120°C	ISO527-2	>100	%

Thermal performance	Test Condition	Test Method	Test Result	Unit
Peak melting temperature		ASTMD3418	220	°C
Hot deformation temperature	0.45MPa,Unannealed	ASTMD648	175	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	150	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	65.0	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	60.0	°C
Melting temperature (DSC)		ISO3146	220	°C
RTIElec	0.71mm	UL746	130	°C
	RTIElec	1.3mm	UL746	130	°C
		RTIElec	3.0mm	UL746	130	°C
		RTIElec	RTIElec	6.0mm	UL746	130	°C
Evolution Calendar intelligent importer	0.71mm	UL746	95.0	°C
	Evolution Calendar intelligent importer	1.3mm	UL746	105	°C
		Evolution Calendar intelligent importer	3.0mm	UL746	105	°C
		Evolution Calendar intelligent importer	Evolution Calendar intelligent importer	6.0mm	UL746	105	°C
RTIStr	0.71mm	UL746	95.0	°C
	RTIStr	1.3mm	UL746	105	°C
		RTIStr	3.0mm	UL746	105	°C
		RTIStr	RTIStr	6.0mm	UL746	105	°C
Linear coefficient of thermal expansion	MD	ASTME831	8.3E-05	cm/cm/°C

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179	NoBreak

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ASTMD785	119

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	3.0mm	UL94	V-2
UL flame retardant rating	UL flame retardant rating	6.0mm	UL94	V-2

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.