Water absorption rate

24hr

ASTMD570

%

1

Water absorption rate

23°C,24hr

ISO62

%

1

Water absorption rate

饱和

ASTMD570

%

9

Water absorption rate

饱和,23°C

ISO62

%

9

Water absorption rate

平衡,23°C,50%RH

ISO62

%

2

Water absorption rate

平衡,50%RH

ASTMD570

%

2

Nominal tensile fracture strain

-40°C

ISO527-2

%

8

Nominal tensile fracture strain

23°C

ISO527-2

%

2

Nominal tensile fracture strain

120°C

ISO527-2

%

>

Tensile strength

屈服,-40°C

ASTMD638

Mpa

1

Tensile strength

屈服,23°C

ASTMD638

Mpa

8

Tensile strength

Yield,121°C

ASTMD638

Mpa

2

Tensile modulus

23°C

ISO527-2

Mpa

2

Tensile strain

屈服,23°C

ISO527-2

%

5

Tensile stress

屈服,-40°C

ISO527-2

Mpa

1

Tensile stress

屈服,23°C

ISO527-2

Mpa

8

Tensile stress

屈服,120°C

ISO527-2

Mpa

2

elongation

屈服,-40°C

ASTMD638

%

3

elongation

屈服,23°C

ASTMD638

%

2

elongation

断裂,-40°C

ASTMD638

%

8

elongation

断裂,23°C

ASTMD638

%

6

elongation

Break,121°C

ASTMD638

%

>

elongation

Yield,121°C

ASTMD638

%

1

Bending modulus

-40°C

ASTMD790

Mpa

3

Bending modulus

23°C

ASTMD790

Mpa

2

Bending modulus

65°C

ASTMD790

Mpa

4

Bending modulus

90°C

ASTMD790

Mpa

3

Bending modulus

121°C

ASTMD790

Mpa

3

Bending modulus

23°C

ISO178

Mpa

2

bending strength

-40°C

ASTMD790

Mpa

1

bending strength

23°C

ASTMD790

Mpa

1

bending strength

65°C

ASTMD790

Mpa

3

bending strength

90°C

ASTMD790

Mpa

2

bending strength

121°C

ASTMD790

Mpa

1

Bending stress

23°C

ISO178

Mpa

8

RTIElec

0.71mm

UL746

°C

1

RTIElec

1.3mm

UL746

°C

1

RTIElec

3.0mm

UL746

°C

1

RTIElec

6.0mm

UL746

°C

1

Evolution Calendar intelligent importer

0.71mm

UL746

°C

9

Evolution Calendar intelligent importer

1.3mm

UL746

°C

1

Evolution Calendar intelligent importer

3.0mm

UL746

°C

1

Evolution Calendar intelligent importer

6.0mm

UL746

°C

1

RTIStr

0.71mm

UL746

°C

9

RTIStr

1.3mm

UL746

°C

1

RTIStr

3.0mm

UL746

°C

1

RTIStr

6.0mm

UL746

°C

1

Hot deformation temperature

0.45MPa,未退火

ASTMD648

°C

1

Hot deformation temperature

0.45MPa,未退火

ISO75-2/B

°C

1

Hot deformation temperature

1.8MPa,未退火

ASTMD648

°C

6

Hot deformation temperature

1.8MPa,未退火

ISO75-2/A

°C

6

Melting temperature (DSC)

ISO3146

°C

2

Peak melting temperature

ASTMD3418

°C

2

Linear coefficient of thermal expansion

MD

ASTME831

cm/cm/°C

8