PA6 Durethan® BKV140H2.0 900051 LANXESS GERMANY
109
- Unit Price:
- $2832 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 45MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.46 |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD:280°C,2.00mm2 | ISO294-4 | 0.75 | % |
| TD:120°C,2hr,2.00mm3 | ISO294-4 | 0.090 | % | |
| MD:280°C,2.00mm2 | ISO294-4 | 0.21 | % | |
| MD:120°C,2hr,2.00mm3 | ISO294-4 | 0.070 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2/1 | 12000 | Mpa |
| Tensile stress | Break,23°C | ISO527-2/5 | 185 | Mpa |
| Tensile strain | Break,23°C | ISO527-2/5 | 3.4 | % |
| Bending modulus 4 | 23°C | ISO178/A | 11000 | Mpa |
| Bending stress 4 | 3.5%Strain | ISO178/A | 280 | Mpa |
| 23°C | ISO178 | 290 | Mpa | |
| FlexuralStrainatFlexuralStrength5(23°C) | 4.2 | % | ||
| Tensile modulus | ASTM D638/ISO 527 | 11200 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 174 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 10400 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 280 | kg/cm²(MPa)[Lb/in²] |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | HB | ||
| vicat softening point | ASTM D1525/ISO R306 | 200 | ℃（℉） | |
| Melting temperature 5 | ISO11357-3 | 220 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 217 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 201 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 100 | kJ/m² |
| 23°C | ISO179/1eU | 110 | kJ/m² | |
| Unscented Izod impact strength | -30°C | ISO180/1U | 90 | kJ/m² |
| 23°C | ISO180/1U | 90 | kJ/m² |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut | ISO1874 | PA6HI,GR,14-120,GF40 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.