PA6/LANXESS GERMANY/BKV140H2.0 900051
Shrinkage rate
TD:280°C,2.00mm2
ISO294-4
%
0
Shrinkage rate
TD:120°C,2hr,2.00mm3
ISO294-4
%
0
Shrinkage rate
MD:280°C,2.00mm2
ISO294-4
%
0
Shrinkage rate
MD:120°C,2hr,2.00mm3
ISO294-4
%
0
Mechanical performance
Test Condition
Test Method
Unit
PA6/LANXESS GERMANY/BKV140H2.0 900051
Tensile modulus
23°C
ISO527-2/1
Mpa
1
Tensile modulus
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
Tensile strain
断裂,23°C
ISO527-2/5
%
3
Tensile stress
断裂,23°C
ISO527-2/5
Mpa
1
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
1
Bending modulus 4
23°C
ISO178/A
Mpa
1
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
Bending stress 4
3.5%Strain
ISO178/A
Mpa
2
Bending stress 4
23°C
ISO178
Mpa
2
Thermal performance
Test Condition
Test Method
Unit
PA6/LANXESS GERMANY/BKV140H2.0 900051
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Melting temperature 5
ISO11357-3
°C
2
vicat softening point
ASTM D1525/ISO R306
℃（℉）
2
Impact performance
Test Condition
Test Method
Unit
PA6/LANXESS GERMANY/BKV140H2.0 900051
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
1
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
1
Unscented Izod impact strength
-30°C
ISO180/1U
kJ/m²
9
Unscented Izod impact strength
23°C
ISO180/1U
kJ/m²
9