Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.36 | |
| Water absorption rate 23 ℃/24h | | ASTM D570/ISO 62 | 1.1 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD:3.00mm3 | % | 0.50到0.80 | -- |
| Shrinkage rate | MD:3.00mm4 | % | 0.20到0.40 | -- |
| Water absorption rate | 23°C,24hr | % | 1.1 | -- |
| Water absorption rate | Saturation,23°C | % | 6.4 | -- |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | | ASTM D785 | R120,M93 | |
| Tensile stress | 80°C | MPa | 100 | 70.0 |
| Tensile strain | Break,-40°C | % | 3.0 | 3.0 |
| Tensile strain | Break,23°C | % | 3.0 | 4.0 |
| Tensile strain | Break,80°C | % | 4.0 | |
| Bending modulus | -40°C | MPa | 11800 | 9800 |
| Bending modulus | 23°C | MPa | 9500 | 5100 |
| Bending modulus | 80°C | MPa | 4700 | 3500 |
| Bending stress | -40°C | MPa | 325 | 315 |
| Bending stress | 23°C | MPa | 280 | 145 |
| Bending stress | 80°C | MPa | 155 | 105 |
| Tensile stress | -40°C | MPa | 250 | 225 |
| Tensile stress | 23°C | MPa | 185 | 105 |
| Compressive stress | -40°C | MPa | 250 | 210 |
| Compressive stress | 23°C | MPa | 180 | |
| Compressive stress | 80°C | MPa | 95.0 | 70.0 |
| shear strength | 23°C | MPa | 85.0 | -- |
| Taber abraser | 1000Cycles | mg | 0.350 | -- |
| Friction coefficient vs. Metal5 | | | 0.15 | -- |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,Unannealed | °C | 224 | -- |
| Melting temperature | | °C | 225 | -- |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 2.0E-5到3.0E-5 | -- |
| specific heat | | J/kg/°C | 1600 | -- |
| thermal conductivity | | W/m/K | 0.38 | -- |
| melting point | | | 225 | ℃（℉） |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | ASTM D257/IEC 60093 | 10^13 | Ω.cm |
| Dissipation factor 6 | 23°C,50Hz | | 0.030 | 0.17 |
| Dissipation factor 6 | 23°C,1kHz | | 0.030 | 0.18 |
| Dissipation factor 6 | 23°C,1MHz | | 0.030 | 0.070 |
| Arc resistance 7 | | sec | 131 | |
| Volume resistivity | | ohms·cm | 1E+15 | 1E+12 |
| Dielectric strength | | kV/mm | 20 | 18 |
| Dielectric constant 6 | 23°C,50Hz | | 4.90 | 10.7 |
| Dielectric constant 6 | 23°C,1kHz | | 4.60 | 7.90 |
| Dielectric constant 6 | 23°C,1MHz | | 4.00 | 4.30 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of simply supported beam without notch | -40°C | kJ/m² | 70 | |
| Impact strength of simply supported beam without notch | 23°C | kJ/m² | 80 | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M-Sale,23°C | | 93 | -- |
| Rockwell hardness | R-Sale,80°C | | 12 | -- |
| Rockwell hardness | R-Sale,23°C | | 120 | -- |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.79mm | | HB | -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.