PA6 CM1016G-30 TORAY JAPAN
Amilan®
Automotive sector
Glass fiber reinforced
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PA6/TORAY JAPAN/CM1016G-30
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
1
physical property
Test Condition
Test Method
Unit
PA6/TORAY JAPAN/CM1016G-30
Shrinkage rate
TD:3.00mm3
%
--
0
Shrinkage rate
MD:3.00mm4
%
--
0
Water absorption rate
23°C,24hr
%
--
1
Water absorption rate
饱和,23°C
%
--
6
Mechanical performance
Test Condition
Test Method
Unit
PA6/TORAY JAPAN/CM1016G-30
shear strength
23°C
MPa
--
8
Tensile strain
断裂,-40°C
%
3.0
3
Tensile strain
断裂,23°C
%
4.0
3
Tensile stress
-40°C
MPa
225
2
Tensile stress
23°C
MPa
105
1
Tensile stress
80°C
MPa
70.0
1
Taber abraser
1000Cycles
mg
--
0
Bending modulus
-40°C
MPa
9800
1
Bending modulus
23°C
MPa
5100
9
Bending modulus
80°C
MPa
3500
4
Bending stress
-40°C
MPa
315
3
Bending stress
23°C
MPa
145
2
Bending stress
80°C
MPa
105
1
Compressive stress
-40°C
MPa
210
2
Compressive stress
80°C
MPa
70.0
9
Thermal performance
Test Condition
Test Method
Unit
PA6/TORAY JAPAN/CM1016G-30
specific heat
J/kg/°C
--
1
thermal conductivity
W/m/K
--
0
Hot deformation temperature
0.45MPa,未退火
°C
--
2
Melting temperature
°C
--
2
Linear coefficient of thermal expansion
MD
cm/cm/°C
--
2
Electrical performance
Test Condition
Test Method
Unit
PA6/TORAY JAPAN/CM1016G-30
Dielectric strength
kV/mm
18
2
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
1
Volume resistivity
ohms·cm
1E+12
1