PA6 Amilan® CM1001G-15 TORAY JAPAN
173
Unit Price:$2679 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 175MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.25 | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 1.3 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD3：3.00mm | % | 0.70到1.1 | -- |
| Water absorption rate | 23°C,24hr | % | 1.3 | -- |
| Saturation,23°C | % | 8.3 | -- |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus | 23°C | MPa | 5700 | 2700 |
| 80°C | MPa | 2300 | 1700 | |
| Bending stress | -40°C | MPa | 205 | -- |
| 23°C | MPa | 170 | 85.0 | |
| 80°C | MPa | 80.0 | 45.0 | |
| Compressive stress | -40°C | MPa | 205 | 130 |
| 23°C | MPa | 135 | 65.0 | |
| 80°C | MPa | 70.0 | 35.0 | |
| shear strength | 23°C | MPa | 100 | -- |
| Taber abraser | 1000Cycles | mg | 0.300 | -- |
| Friction coefficient vs. Metal4 | 0.15 | -- | ||
| Rockwell hardness | ASTM D785 | R119,M90 | ||
| Tensile stress | -40°C | MPa | 135 | 115 |
| 23°C | MPa | 110 | 55.0 | |
| 80°C | MPa | 45.0 | 25.0 | |
| Tensile strain | Break,-40°C | % | 2.0 | 3.0 |
| Break,23°C | % | 2.0 | ||
| Break,80°C | % | 5.5 | 6.0 | |
| Bending modulus | -40°C | MPa | 7300 | 6000 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| melting point | 225 | ℃（℉） | ||
| Hot deformation temperature | 0.45MPa,Unannealed | °C | 210 | -- |
| Melting temperature | °C | 225 | -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 4.5E-05 | -- |
| specific heat | J/kg/°C | 1700 | -- | |
| thermal conductivity | W/m/K | 0.31 | -- |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ohms·cm | 1E+15 | 1E+12 | |
| Dielectric strength | kV/mm | 20 | -- | |
| Dielectric constant 5 | 23°C,50Hz | 4.50 | -- | |
| 23°C,1kHz | 4.30 | -- | ||
| 23°C,1MHz | 3.70 | -- | ||
| Dissipation factor 5 | 23°C,50Hz | 0.050 | -- | |
| 23°C,1kHz | 0.040 | -- | ||
| 23°C,1MHz | 0.030 | -- | ||
| Arc resistance 6 | sec | 120 | -- | |
| Volume resistivity | ASTM D257/IEC 60093 | 10^13 | Ω.cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | kJ/m² | 20 | 25 |
| 23°C | kJ/m² | 30 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M-Sale,23°C | 90 | -- | |
| R-Sale,80°C | 10 | -- | ||
| R-Sale,23°C | 119 | -- |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.6mm | HB | -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.