Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA6 CM1001G-15 TORAY JAPAN
Amilan®
--
High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PA6/TORAY JAPAN/CM1001G-15
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
1
physical property
Test Condition
Test Method
Unit
PA6/TORAY JAPAN/CM1001G-15
Shrinkage rate
TD3：3.00mm
%
--
0
Water absorption rate
饱和,23°C
%
--
8
Water absorption rate
23°C,24hr
%
--
1
Mechanical performance
Test Condition
Test Method
Unit
PA6/TORAY JAPAN/CM1001G-15
shear strength
23°C
MPa
--
1
Tensile strain
断裂,-40°C
%
3.0
2
Tensile strain
断裂,80°C
%
6.0
5
Tensile stress
-40°C
MPa
115
1
Tensile stress
23°C
MPa
55.0
1
Tensile stress
80°C
MPa
25.0
4
Taber abraser
1000Cycles
mg
--
0
Bending modulus
-40°C
MPa
6000
7
Bending modulus
80°C
MPa
1700
2
Bending modulus
23°C
MPa
2700
5
Bending stress
80°C
MPa
45.0
8
Bending stress
23°C
MPa
85.0
1
Bending stress
-40°C
MPa
--
2
Compressive stress
80°C
MPa
35.0
7
Compressive stress
23°C
MPa
65.0
1
Compressive stress
-40°C
MPa
130
2
Thermal performance
Test Condition
Test Method
Unit
PA6/TORAY JAPAN/CM1001G-15
specific heat
J/kg/°C
--
1
thermal conductivity
W/m/K
--
0
Hot deformation temperature
0.45MPa,未退火
°C
--
2
Melting temperature
°C
--
2
Linear coefficient of thermal expansion
MD
cm/cm/°C
--
4
Electrical performance
Test Condition
Test Method
Unit
PA6/TORAY JAPAN/CM1001G-15
Dielectric strength
kV/mm
--
2
Arc resistance 6
sec
--
1
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
1
Volume resistivity
ohms·cm
1E+12
1
Impact performance
Test Condition
Test Method
Unit
PA6/TORAY JAPAN/CM1001G-15
Impact strength of simply supported beam without notch
-40°C
kJ/m²
25
2