Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt mass flow rate | 230°C/2.16kg | ISO1133 | 2.8 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | Yield | ISO527-2 | 18.0 | Mpa |
| Tensile stress | Break | ISO527-2 | 22.5 | Mpa |
| Tensile strain | Break | ISO527-2 | >500 | % |
| Bending modulus | | ISO178 | 450 | Mpa |
| Bending stress | | ISO178 | 17.5 | Mpa |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| Film thickness - tested | | | 80 | µm |
| Tensile modulus | MD:80µm | JISZ1702 | 430 | Mpa |
| Tensile modulus | TD:80µm | JISZ1702 | 430 | Mpa |
| Tensile stress | MD:Break,80μm | JISZ1702 | 40.0 | Mpa |
| Tensile stress | TD:Break,80μm | JISZ1702 | 40.0 | Mpa |
| elongation | MD:Break,80μm | JISZ1702 | >500 | % |
| elongation | TD:Break,80μm | JISZ1702 | >500 | % |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Unscented Izod impact strength | 23°C | ISO180 | 15 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Shore hardness | Shore D | ASTMD2240 | 67 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Haze | 80.0µm2 | JISK7105 | 11 | % |
| Haze | 80.0µm3 | JISK7105 | 0.60 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.