Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP E-2900 PRIME POLYMER JAPAN
PRIME
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PP/PRIME POLYMER JAPAN/E-2900
Melt mass flow rate
230°C/2.16kg
ISO1133
g/10min
2
Mechanical performance
Test Condition
Test Method
Unit
PP/PRIME POLYMER JAPAN/E-2900
Tensile strain
断裂
ISO527-2
%
>
Tensile stress
屈服
ISO527-2
Mpa
1
Tensile stress
断裂
ISO527-2
Mpa
2
Bending modulus
ISO178
Mpa
4
Bending stress
ISO178
Mpa
1
film
Test Condition
Test Method
Unit
PP/PRIME POLYMER JAPAN/E-2900
Tensile modulus
MD:80µm
JISZ1702
Mpa
4
Tensile modulus
TD:80µm
JISZ1702
Mpa
4
Tensile stress
MD:断裂,80µm
JISZ1702
Mpa
4
Tensile stress
TD:断裂,80µm
JISZ1702
Mpa
4
elongation
MD:断裂,80µm
JISZ1702
%
>
elongation
TD:断裂,80µm
JISZ1702
%
>
Impact performance
Test Condition
Test Method
Unit
PP/PRIME POLYMER JAPAN/E-2900
Unscented Izod impact strength
23°C
ISO180
kJ/m²
1
optical performance
Test Condition
Test Method
Unit
PP/PRIME POLYMER JAPAN/E-2900
Haze
80.0µm2
JISK7105
%
1
Haze
80.0µm3
JISK7105
%
0