ABS TAITALAC® 1000T TAIDA TAIWAN
121
- Unit Price:
- $1629 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 13.1MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High gloss High mobility Fatigue resistance Moderate impact resistanc
- Application Areas:battery Electrical enclosure Electrical appliances TV casing furniture Toy Footwear
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 200℃/5.0 kg | ASTM D1238 | 1.8 | g/10 min |
| 220℃/10.0 kg | ASTM D1238 | 18 | g/10 min | |
| Melt mass flow rate | 200°C/5.0kg | ASTMD1238 | 1.8 | g/10min |
| 220°C/10.0kg | ASTMD1238 | 18 | g/10min | |
| Water absorption rate | Saturation | ASTM D570 | < 0.30 | % |
| Saturation | ASTMD570 | <0.30 | % | |
| Shrinkage rate | MD | ASTM D955 | < 0.40 | % |
| MD | ASTMD955 | <0.40 | % | |
| Density/specific gravity | ASTMD792 | 1.03 | g/cm³ | |
| ASTM D792 | 1.03 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending strength 4 | Yield,23°C | ASTMD790 | 68.9 | Mpa |
| Bending modulus 3 | 23°C | ASTMD790 | 2340 | Mpa |
| Tensile strength 2 | Yield,23°C,3.18mm | ASTMD638 | 40.0 | Mpa |
| Elongation rate 2 | Break,23°C,3.18mm | ASTMD638 | 30 | % |
| Tensile strength 2 | Break,23°C,3.18mm | ASTMD638 | 35.2 | Mpa |
| elongation | Break, 23℃, 3.18 mm | ASTM D638 | 30 | % |
| Rockwell hardness | R-Scale, 23℃ | ASTM D785 | 110 | |
| Bending modulus | 23℃ | ASTM D790 | 2340 | Mpa |
| bending strength | Yield, 23℃ | ASTM D790 | 68.9 | Mpa |
| Tensile strength | Yield, 23℃, 3.18 mm | ASTM D638 | 40 | Mpa |
| Break, 23℃, 3.18 mm | ASTM D638 | 35.2 | Mpa | |
| Impact strength of cantilever beam gap | 23℃, 3.18 mm | ASTM D256 | 260 | J/m |
| 23℃, 6.35 mm | ASTM D256 | 230 | J/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | ASTM D1525 | 103 | °C | |
| Hot deformation temperature | 1.8 MPa, Annealed, 12.7 mm | ASTM D648 | 86 | °C |
| 1.8MPa,Annealed,12.7mm | ASTMD648 | 86.0 | °C | |
| Flame retardant grade | 1.59 mm | UL 94 | HB | |
| RTIElec | 1.6mm | UL746 | 60.0 | °C |
| Evolution Calendar intelligent importer | 1.6mm | UL746 | 60.0 | °C |
| RTIStr | 1.6mm | UL746 | 60.0 | °C |
| High arc combustion index | 1.57 mm | UL 746 | 200 | |
| High voltage arc tracing rate | 1.57 mm | UL 746 | 0.00 | mm/min |
| Hot wire ignition | 1.57 mm | UL 746 | 17 | sec |
| Vicat softening temperature 4 | ASTMD15255 | 103 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| High arc combustion index | 1.57mm | UL746 | 200 | |
| High voltage arc ignition resistance index | 1.57mm | UL746 | 0.00 | mm/min |
| Hot-wireIgnition | 1.57mm | UL746 | 17 | sec |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C,3.18mm | ASTMD256 | 260 | J/m |
| 23°C,6.35mm | ASTMD256 | 230 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Sale,23°C | ASTMD785 | 110 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 1.6mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.