ABS 1000T TAIDA TAIWAN
TAITALAC®
battery、Electrical enclosure、Electrical appliances、TV casing、furniture、Toy、Footwear、battery、Electrical enclosure、Electrical appliances、TV casing、furniture、Toy、Footwear
High gloss、High mobility、Fatigue resistance、Moderate impact resistanc
UL
TDS
TDS_ISO
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | TAIDA TAIWAN/1000T |
|---|---|---|---|
| Vicat Softening Temperature | ASTMD15255 | 103 °C | |
| Heat Deflection Temperature | 1.8 MPa, 退火, 12.7 mm | ASTM D648 | 86 °C |
| Vicat Softening Temperature | ASTM D1525 | 103 °C | |
| High Amp Arc Ignition | 1.57 mm | UL 746 | 200 |
| Heat Deflection Temperature | 1.8MPa,Annealed,12.7mm | ASTMD648 | 86.0 °C |
| RTIElec | 1.6mm | UL746 | 60.0 °C |
| RTIStr | 60.0 °C | ||
| Hot-wire Ignition | 1.57 mm | UL 746 | 17 sec |
| Flame retardant grade | 1.59 mm | UL 94 | HB |
| Evolution Calendar intelligent importer | 1.6mm | UL746 | 60.0 °C |
| High Voltage Arc Tracking Rate | 1.57 mm | UL 746 | 0.00 mm/min |
| Hardness | Test Condition | Test Method | TAIDA TAIWAN/1000T |
|---|---|---|---|
| Rockwell Hardness | R计秤,23°C | ASTMD785 | 110 |
| Mechanical Properties | Test Condition | Test Method | TAIDA TAIWAN/1000T |
|---|---|---|---|
| Tensile Strength | 屈服,23°C,3.18mm | ASTMD638 | 40.0 Mpa |
| Flexural Modulus | 23℃ | ASTM D790 | 2340 Mpa |
| Tensile Strength | 断裂, 23℃, 3.18 mm | ASTM D638 | 35.2 Mpa |
| 屈服, 23℃, 3.18 mm | 40 Mpa | ||
| Tensile Elongation | 断裂,23°C,3.18mm | ASTMD638 | 30 % |
| Flexural Strength | 屈服,23°C | ASTMD790 | 68.9 Mpa |
| 屈服, 23℃ | ASTM D790 | 68.9 Mpa | |
| Rockwell Hardness | R 级, 23℃ | ASTM D785 | 110 |
| Tensile Elongation | 断裂, 23℃, 3.18 mm | ASTM D638 | 30 % |
| Notched Izod Impact Strength | 23℃, 3.18 mm | ASTM D256 | 260 J/m |
| Flexural Modulus | 23°C | ASTMD790 | 2340 Mpa |
| Tensile Strength | Break,23°C,3.18mm | ASTMD638 | 35.2 Mpa |
| Notched Izod Impact Strength | 23℃, 6.35 mm | ASTM D256 | 230 J/m |
| Physical | Test Condition | Test Method | TAIDA TAIWAN/1000T |
|---|---|---|---|
| Melt Mass-Flow Rate | 220℃/10.0 kg | ASTM D1238 | 18 g/10 min |
| Moisture Absorption | 饱和 | ASTM D570 | < 0.30 % |
| Density / Specific Gravity | ASTM D792 | 1.03 g/cm³ | |
| Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 18 g/10min |
| Density / Specific Gravity | ASTMD792 | 1.03 g/cm³ | |
| Melt Mass-Flow Rate | 200℃/5.0 kg | ASTM D1238 | 1.8 g/10 min |
| 200°C/5.0kg | ASTMD1238 | 1.8 g/10min | |
| Modeling Shrinkage | MD | ASTM D955 | < 0.40 % |
| Moisture Absorption | 饱和 | ASTMD570 | <0.30 % |
| Modeling Shrinkage | MD | ASTMD955 | <0.40 % |
| Impact Properties | Test Condition | Test Method | TAIDA TAIWAN/1000T |
|---|---|---|---|
| Notched Izod Impact Strength | 23°C,6.35mm | ASTMD256 | 230 J/m |
| 23°C,3.18mm | 260 J/m |
| Flammability | Test Condition | Test Method | TAIDA TAIWAN/1000T |
|---|---|---|---|
| Flame Rating | 1.6mm | UL94 | HB |
| Electrical Properties | Test Condition | Test Method | TAIDA TAIWAN/1000T |
|---|---|---|---|
| High Amp Arc Ignition | 1.57mm | UL746 | 0.00 mm/min |
| 200 | |||
| Hot-wireIgnition | 17 sec |