ABS CYCOLAC™ BDT5510-1000 SABIC INNOVATIVE US
117
- Unit Price:
- $3391 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 11MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low gloss
- Application Areas:Automotive sector Automotive interior parts
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 220°C/10.0kg | ISO1133 | 14 | g/10min |
| 230°C/3.8kg | ASTMD1238 | 6.0 | g/10min | |
| SpiralFlow2.3 | 内部方法 | 73.7 | CM | |
| Melt viscosity | 260°C,1000sec^-1 | ASTMD3835 | 163 | Pa·s |
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.50to0.80 | % |
| Density/specific gravity | ASTMD792 | 1.05 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Yield | ISO527-2/50 | 43.0 | Mpa |
| Tensile modulus | ISO527-2/1 | 2930 | Mpa | |
| Bending modulus 7 | 50.0mmSpan | ASTMD790 | 2460 | Mpa |
| ISO178 | 2030 | Mpa | ||
| Bending strength 7,8 | ISO178 | 67.0 | Mpa | |
| Bending strength 7 | Yield,50.0mmSpan | ASTMD790 | 81.0 | Mpa |
| Tensile modulus 4 | ASTMD638 | 2280 | Mpa | |
| Tensile strength 6 | Yield | ASTMD638 | 53.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 81.0 | °C |
| 0.45MPa,Unannealed,3.20mm | ASTMD648 | 92.0 | °C | |
| Vicat softening temperature | ISO306/B50 | 98.0 | °C | |
| Linear coefficient of thermal expansion | MD：-40to60°C | ASTME831 | 1.4E-04 | cm/cm/°C |
| Hot deformation temperature 11 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 83.0 | °C |
| 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 95.0 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 290 | J/m |
| Falling hammer impact | 23°C | ASTMD3029 | 35.0 | J |
| Impact strength of simply supported beam gap 9 | 23°C | ISO179/1eA | 13 | kJ/m² |
| -30°C | ISO179/1eA | 7.2 | kJ/m² | |
| Suspended wall beam gap impact strength 10 | 23°C | ISO180/1A | 13 | kJ/m² |
| -30°C | ISO180/1A | 7.0 | kJ/m² |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Gardner glossiness | 60°,无织构 | ASTMD523 | 25 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.