ABS BDT5510-1000 SABIC INNOVATIVE US
CYCOLAC™
Automotive sector、Automotive interior parts
Low gloss
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE US/BDT5510-1000
SpiralFlow2.3
内部方法
CM
7
Density/specific gravity
ASTMD792
g/cm³
1
Melt viscosity
260°C,1000sec^-1
ASTMD3835
Pa·s
1
Melt mass flow rate
230°C/3.8kg
ASTMD1238
g/10min
6
Melt mass flow rate
220°C/10.0kg
ISO1133
g/10min
1
Shrinkage rate
MD：3.20mm
内部方法
%
0
Mechanical performance
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE US/BDT5510-1000
Tensile strength 6
屈服
ASTMD638
Mpa
5
Tensile modulus
ISO527-2/1
Mpa
2
Tensile modulus 4
ASTMD638
Mpa
2
Tensile stress
屈服
ISO527-2/50
Mpa
4
Bending modulus 7
50.0mm跨距
ASTMD790
Mpa
2
Bending modulus 7
ISO178
Mpa
2
Bending strength 7
屈服,50.0mm跨距
ASTMD790
Mpa
8
Bending strength 7,8
ISO178
Mpa
6
Thermal performance
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE US/BDT5510-1000
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
9
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
8
Hot deformation temperature 11
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
8
Hot deformation temperature 11
0.45MPa,Unannealed,64.0mmSpan
ISO75-2/Bf
°C
9
Vicat softening temperature
ISO306/B50
°C
9
Linear coefficient of thermal expansion
MD：-40到60°C
ASTME831
cm/cm/°C
1
Impact performance
Test Condition
Test Method
Unit
ABS/SABIC INNOVATIVE US/BDT5510-1000
Impact strength of simply supported beam gap 9
-30°C
ISO179/1eA
kJ/m²
7
Impact strength of simply supported beam gap 9
23°C
ISO179/1eA
kJ/m²
1
Falling hammer impact
23°C
ASTMD3029
J
3
Impact strength of cantilever beam gap
23°C
ASTMD256
J/m
2
Suspended wall beam gap impact strength 10
-30°C
ISO180/1A
kJ/m²
7
Suspended wall beam gap impact strength 10
23°C
ISO180/1A
kJ/m²
1