ABS Toyolac® 920 TORAY JAPAN
197
- Unit Price:
- $2623 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 68.6MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility High rigidity transparent
- Application Areas:Electrical field Electronic field Automotive sector sporting goods small home appliances Lighting fixtures
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index (flow coefficient) | ASTM D1238/ISO 1133 | 25 | g/10min | |
| density | ASTM D792/ISO 1183 | 1.09 |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 220℃/10kg | ISO 1133 | 25 | g/10min |
| Water absorption | 浸入23℃水中24hr | ASTM D-570 | 0.3 | % |
| Melt index | 220℃ 10kg | ASTM D-1238 | 19～23 | g/10min |
| Combustibility | UL-94 | 94HB | ||
| Melt viscosity | 220℃ | 3.5～5.0 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| yield strength | 23℃ | ASTM D-638 | 490 | kg/cm |
| Rockwell hardness | 23℃ | ASTM D-785 | 115 | R |
| Tensile strength under yield | 23℃ | ASTM D-638 | 3.5 | % |
| Tensile strength at break | 23℃ | ASTM D-638 | 30 | % |
| Flexural limit | 23℃ | ASTM D-790 | 23500 | kg/cm |
| impact strength | 12.7×12.7×62.5mm(带韧口)，23℃；0℃；-30℃ | ASTM D-256 | 9；7；6 | kg.cm/cm |
| 3.2×12.7×62.5mm(带韧口)，23℃；0℃；-30℃ | ASTM D-256 | 10；7；6 | kg.cm/cm | |
| Flexural strength | 23℃ | ASTM D-790 | 780 | kg/cm |
| Fracture strength | 23℃ | ASTM D-638 | 380 | kg/cm |
| Tensile yield stress | 23℃ | ISO 527-2 | 54.0 | Mpa |
| Tensile fracture strain | 23℃ | ISO 527-2 | 17 | % |
| elongation at break | ASTM D638/ISO 527 | 20 | % | |
| tensile strength | ASTM D638/ISO 527 | 48 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 115 | ||
| Bending modulus | ASTM D790/ISO 178 | 2160 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 74 | kg/cm²(MPa)[Lb/in²] | |
| IZOD notch impact strength | ASTM D256/ISO 179 | 108 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 83 | ℃（℉） | |
| Linear expansion coefficient | ASTM D-696 | 1.2×10 | mm/mm/℃ | |
| Hot deformation temperature | 18.56kg/cm | ASTM D-648 | 89 | °C |
| 1.8MPa，Unannealed | ISO 75-2/A | 77.0 | °C | |
| UL flame retardant rating | UL 94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.