Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 920 TORAY JAPAN
Toyolac®
Electrical field、Electronic field、Automotive sector、sporting goods、small home appliances、Lighting fixtures
High mobility、High rigidity、transparent
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
ABS/TORAY JAPAN/920
Melt index (flow coefficient)
ASTM D1238/ISO 1133
g/10min
2
physical property
Test Condition
Test Method
Unit
ABS/TORAY JAPAN/920
Melt index
220℃ 10kg
ASTM D-1238
g/10min
1
Melt index
220℃/10kg
ISO 1133
g/10min
2
Water absorption
浸入23℃水中24小时
ASTM D-570
%
0
Mechanical performance
Test Condition
Test Method
Unit
ABS/TORAY JAPAN/920
impact strength
12.7×12.7×62.5mm(带韧口)，23℃；0℃；-30℃
ASTM D-256
kg.cm/cm
9
impact strength
3.2×12.7×62.5mm(带韧口)，23℃；0℃；-30℃
ASTM D-256
kg.cm/cm
1
Fracture strength
23℃
ASTM D-638
kg/cm
3
Tensile strength at break
23℃
ASTM D-638
%
3
elongation at break
ASTM D638/ISO 527
%
2
Tensile fracture strain
23℃
ISO 527-2
%
1
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
4
Tensile yield stress
23℃
ISO 527-2
Mpa
5
Rockwell hardness
23℃
ASTM D-785
R
1
Flexural limit
23℃
ASTM D-790
kg/cm
2
Flexural strength
23℃
ASTM D-790
kg/cm
7
yield strength
23℃
ASTM D-638
kg/cm
4
Tensile strength under yield
23℃
ASTM D-638
%
3
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
7
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
1
Thermal performance
Test Condition
Test Method
Unit
ABS/TORAY JAPAN/920
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
8
Hot deformation temperature
18.56kg/cm
ASTM D-648
°C
8
Hot deformation temperature
1.8MPa，未退火
ISO 75-2/A
°C
7
Linear expansion coefficient
ASTM D-696
mm/mm/℃
1