PC/ABS CYCOLOY™ CY4000-7M1A4447 SABIC INNOVATIVE NANSHA
114
- Unit Price:
- $4924 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high strength Aging resistance
- Application Areas:Electronic and electrical Shell
- Color:--
- Grade:High liquidity level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 260℃ 2.16kg | ASTM D1238 | 23 | g/10min |
| 260℃ 2.16kg | ISO 1133 | 21 | g/10min | |
| proportion | ISO 1183 | 1.2 | g/cm³ | |
| Vertical shrinkage rate | ISO 294 | 0.6 | % | |
| Shrinkage rate flow | ISO 294 | 0.4 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Cantilever beam gap impact | 23℃ | ISO 180 | 10 | kJ/m² |
| -30℃ | ISO 180 | 10 | kJ/m² | |
| Vertical coefficient of linear color expansion | ISO 11359 | 0.000080 | cm/cm/℃ | |
| Tiber wear and tear | 1kg | 15 | mg/1000cy | |
| Hot deformation temperature | Unannealed0.45MPa | ISO 75 | 85 | °C |
| Unannealed1.8MPa | ISO 75 | 72 | °C | |
| Impact of simply supported beam gap | 23℃ | ISO 179 | 10 | kJ/m² |
| -30℃ | ISO 179 | 10 | kJ/m² | |
| Vicat softening temperature | 50℃/hr 50N | ISO 306 | 85 | °C |
| 120℃/hr 50N | ISO 306 | 90 | °C | |
| Tensile modulus | 23℃ | ISO 527 | 2700 | Mpa |
| tensile strength | Yield23℃ | ISO 527 | 55 | Mpa |
| 23℃ 50mm/min | ISO 527 | 45 | Mpa | |
| elongation | Yield23℃ 50mm/min | ISO 527 | 3 | % |
| 23℃ | ISO 527 | 40 | % | |
| Bending modulus | 23℃ | ISO 178 | 2500 | Mpa |
| bending strength | Yield23℃ | ISO 178 | 85 | Mpa |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric constant | 1MHz | IEC 60250 | 2.7 | |
| IEC 60250 | 2.7 | |||
| Insulation strength | 3.2mm | IEC 60243 | 17 | KV/mm |
| Volume resistance | IEC 60093 | 1000000000000000 | Ω.cm | |
| Surface resistance | IEC 60093 | 1000000000000000 | ||
| CTI | IEC 60112 | 600 | V | |
| Dispersion factor 1MHz | IEC 60250 | 0.006 | ||
| Dispersion factor | IEC 60250 | 0.006 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | H358/30 | ISO 2039 | 110 | Mpa |
| Flame retardant performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative temperature of heating wire | 3.2mm | IEC 60695 | 960 | °C |
| Extreme Oxygen Index | ISO 4589 | 29 | % | |
| Fire rating | 2.5mm | UL94 | V-0 | |
| 3.0mm | UL94 | V-0 |
| UL | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTI Day EC | 2.5mm | UL746B | 60 | °C |
| Fire rating | 2.5mm | UL94 | V-0 | |
| 3.0mm | UL94 | V-0 | ||
| RTI Elec | 3.0mm | UL 746B | 60 | °C |
| RTI Imp | 2.5mm | UL746B | 60 | °C |
| 3.0mm | UL746B | 60 | °C | |
| RTI Str | 2.5mm | UL746B | 60 | °C |
| 3.0mm | UL746B | 60 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.