Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS CY4000-7M1A4447 SABIC INNOVATIVE NANSHA
CYCOLOY™
Electronic and electrical、Shell
high strength、Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CY4000-7M1A4447
proportion
ISO 1183
g/cm³
1
Melt index
260℃ 2.16kg
ASTM D1238
g/10min
2
Melt index
260℃ 2.16kg
ISO 1133
g/10min
2
Vertical shrinkage rate
ISO 294
%
0
Shrinkage rate flow
ISO 294
%
0
Mechanical performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CY4000-7M1A4447
Impact of simply supported beam gap
23℃
ISO 179
kJ/m²
1
Impact of simply supported beam gap
-30℃
ISO 179
kJ/m²
1
Tensile modulus
23℃
ISO 527
Mpa
2
tensile strength
屈服23℃
ISO 527
Mpa
5
tensile strength
23℃ 50mm/min
ISO 527
Mpa
4
Hot deformation temperature
未退火0.45MPa
ISO 75
°C
8
Hot deformation temperature
未退火1.8MPa
ISO 75
°C
7
elongation
屈服23℃ 50mm/min
ISO 527
%
3
elongation
23℃
ISO 527
%
4
Bending modulus
23℃
ISO 178
Mpa
2
bending strength
屈服23℃
ISO 178
Mpa
8
Vicat softening temperature
50℃/hr 50N
ISO 306
°C
8
Vicat softening temperature
120℃/hr 50N
ISO 306
°C
9
Vertical coefficient of linear color expansion
ISO 11359
cm/cm/℃
0
Cantilever beam gap impact
23℃
ISO 180
kJ/m²
1
Cantilever beam gap impact
-30℃
ISO 180
kJ/m²
1
Electrical performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CY4000-7M1A4447
CTI
IEC 60112
V
6
Insulation strength
3.2mm
IEC 60243
KV/mm
1
Volume resistance
IEC 60093
Ω.cm
1
hardness
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CY4000-7M1A4447
Ball pressure hardness
H358/30
ISO 2039
Mpa
1
Flame retardant performance
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CY4000-7M1A4447
Extreme Oxygen Index
ISO 4589
%
2
Relative temperature of heating wire
3.2mm
IEC 60695
°C
9
UL
Test Condition
Test Method
Unit
PC/ABS/SABIC INNOVATIVE NANSHA/CY4000-7M1A4447
RTI Elec
3.0mm
UL 746B
°C
6
RTI Imp
2.5mm
UL746B
°C
6
RTI Imp
3.0mm
UL746B
°C
6
RTI Str
2.5mm
UL746B
°C
6
RTI Str
3.0mm
UL746B
°C
6
RTI Day EC
2.5mm
UL746B
°C
6