PPO XYRON™ 100Z ASAHI JAPAN

124

Unit Price:
$3506 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Chemical resistance Low temperature resistanc
Application Areas:Electrical tools Sports Equipment
Color:--
Grade:Injection grade

Technical Data Sheet Compare

Physical properties	Test Condition	Test Method	Test Result	Unit
density		ASTM D792/ISO 1183	1.08
Water absorption rate 23 ℃/24h		ASTM D570/ISO 62	0.1	%

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	2.00mm	内部方法	0.50to0.70	%
Water absorption rate	23°C,24hr	ISO62	0.10	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress	Yield,23°C	ISO527-2	37.0	Mpa
Nominal tensile fracture strain	23°C	ISO527-2	30	%
Bending modulus	23°C	ISO178	2370	Mpa
Bending stress	23°C	ISO178	66.0	Mpa
elongation at break		ASTM D638/ISO 527	40	%
tensile strength		ASTM D638/ISO 527	36	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	R110
Bending modulus		ASTM D790/ISO 178	2250	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	59	kg/cm²(MPa)[Lb/in²]
Tensile stress		ASTM D-638	39	Mpa
Elongation rate		ASTM D-638	40	%
Bending modulus		ASTM D-790	2350	Mpa
bending strength		ASTM D-790	59	Mpa
Flame retardant grade		UL 94	V-0

Thermal performance	Test Condition	Test Method	Test Result	Unit
Combustibility (rate)		UL94	V-0
Hot deformation temperature		ASTM D648/ISO 75	85	℃（℉）
	Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	85.0	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	78.0	°C
Linear coefficient of thermal expansion	MD：-30to65°C	ISO11359-2	8E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC60093	1E+16	ohms
Volume resistivity	23°C	IEC60093	1E+16	ohms·cm
Dielectric strength 5	2.00mm	IEC60243-1	29	KV/mm
Dielectric constant	100Hz	IEC60250	2.90
Dielectric constant	Dielectric constant	1MHz	IEC60250	2.90
Dissipation factor	100Hz	IEC60250	3E-03
Dissipation factor	Dissipation factor	1MHz	IEC60250	4E-03

Processing performance	Test Condition	Test Method	Test Result	Unit
Mold temperature			40-70	°C

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam gap 3	23°C	ISO179	16	kJ/m²

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5mm	UL94	V-0
UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	5VA

Basic performance	Test Method	Test Result	Unit
density	ASTM D-792	1.08	g/cm
Shrinkage rate	ASTM D-955	0.50-0.70	%
Water absorption rate	ASTM D-570	0.10	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.