Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO 100Z ASAHI JAPAN
XYRON™
Electrical tools、Sports Equipment
Chemical resistance、Low temperature resistanc
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PPO/ASAHI JAPAN/100Z
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
0
physical property
Test Condition
Test Method
Unit
PPO/ASAHI JAPAN/100Z
Shrinkage rate
2.00mm
内部方法
%
0
Water absorption rate
23°C,24hr
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPO/ASAHI JAPAN/100Z
Nominal tensile fracture strain
23°C
ISO527-2
%
3
elongation at break
ASTM D638/ISO 527
%
4
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
3
Tensile stress
ASTM D-638
Mpa
3
Tensile stress
屈服,23°C
ISO527-2
Mpa
3
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
Bending modulus
ASTM D-790
Mpa
2
Bending modulus
23°C
ISO178
Mpa
2
bending strength
ASTM D-790
Mpa
5
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
5
Bending stress
23°C
ISO178
Mpa
6
Elongation rate
ASTM D-638
%
4
Thermal performance
Test Condition
Test Method
Unit
PPO/ASAHI JAPAN/100Z
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
8
Hot deformation temperature
1.8MPa,未退火
ASTMD648
°C
8
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
7
Linear coefficient of thermal expansion
MD：-30到65°C
ISO11359-2
cm/cm/°C
8
Electrical performance
Test Condition
Test Method
Unit
PPO/ASAHI JAPAN/100Z
Surface resistivity
IEC60093
ohms
1
Dielectric strength 5
2.00mm
IEC60243-1
KV/mm
2
Volume resistivity
23°C
IEC60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PPO/ASAHI JAPAN/100Z
Impact strength of simply supported beam gap 3
23°C
ISO179
kJ/m²
1
Basic performance
Test Condition
Test Method
Unit
PPO/ASAHI JAPAN/100Z
density
ASTM D-792
g/cm
1
Shrinkage rate
ASTM D-955
%
0
Water absorption rate
ASTM D-570
%
0