POK POKETONE™ M330F HYOSUNG KOREA
257
- Unit Price:
- $3129 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 310MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility High impact resistance High chemical resistance High wear resistance High gas barrier High flame retardancy
- Application Areas:Electronic appliances Industrial materials automobile
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shore hardness | ISO 868 | 77 | ||
| Rockwell hardness | ASTM D785 | 110 | ||
| Water absorption rate | Equilibrium，50%RH | ASTM D570,ISO 62 | 0.5 | % |
| Saturation | ASTM D570,ISO 62 | 2.1 | % | |
| Melt mass flow rate | 240℃，2.16kg | ASTM D1238 | 60 | g/10min |
| 240℃，2.16kg | ISO 1133 | 56 | ||
| Shrinkage rate | MD, 3 mm | ASTM D955 | 2 | % |
| TD, 3 mm | ASTM D955 | 2 | % | |
| MD, 2 mm | ASTM D955 | 1.6 | % | |
| TD, 2 mm | ASTM D955 | 1.5 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Yield | ASTM D638,ISO 527-1 | 60 | Mpa |
| Tensile modulus | ASTM D638 | 1600 | Mpa | |
| ISO 527-1 | 1500 | Mpa | ||
| Tensile yield elongation | ASTM D638,ISO 527-1 | 21 | % | |
| Tensile elongation at break | ASTM D638,ISO 527-1 | 300 | % | |
| Bending strength | ASTM D790,ISO 178 | 57 | Mpa | |
| Bending modulus | ASTM D790 | 1500 | ||
| ISO 178 | 1400 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature | ASTM D955,ISO 11357 | 222 | °C | |
| Linear coefficient of thermal expansion | 25℃ to 55℃ | ASTM E831 | 0.000097 | |
| Vicat softening point | 5 kg | ASTM D-1525 | 195 | °C |
| 50 N | ISO 306/B50 | 190 | °C | |
| Hot deformation temperature | 66psi | ASTM D648 | 200 | °C |
| 264psi | ASTM D648 | 105 | °C | |
| 0.45 MPa | ISO 75 | 190 | °C | |
| 1.8 MPa | ISO 75 | 92 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 短期，3 mm | ASTM D149 | 15 | KV/mm |
| 短期，2 mm | ASTM D149 | 19 | KV/mm | |
| Volume resistivity | ASTM D257 | 1000000000000000 | ohms·cm | |
| Surface resistivity | ASTM D257 | 1000000000000000000 | ohm/sq | |
| Arc resistance | ASTM D495 | 130 | sec | |
| Compared to the leakage trace index | IEC 112 | 600 | V | |
| Dielectric constant | 60Hz | ASTM D150 | 6.2 | |
| 60Hz | IEC 250 | 5 | ||
| Dissipation factor | 60Hz | ASTM D150 | 0.008 | |
| 60Hz | IEC 250 | 0.013 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Cantilever beam without notch impact strength | ASTM D256,ISO 180/1U | N.B. | ||
| Impact strength of cantilever beam gap | 23℃ | ASTM D256 | 95 | kJ/m² |
| 23℃ | ISO 180/1A | 7 | kJ/m² | |
| -10℃ | ASTM D256 | 60 | kJ/m² | |
| -10℃ | ISO 180/1A | 4 | kJ/m² | |
| -30℃ | ASTM D256 | 40 | kJ/m² | |
| -30℃ | ISO 180/1A | 3 | kJ/m² | |
| Falling hammer impact | 23℃ | ISO 6603-2 | 50 | J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.