PC/ASA GELOY™ XTPMFR10-1000 SABIC INNOVATIVE NANSHA
104
- Unit Price:
- $3074 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Antistatic High mobility
- Application Areas:Electrical applications Automotive Applications
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Molten Volume Flow Rate (MVR) | 260°C/2.16 kg | ISO 1133 | 30.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | -- 2 | ASTM D638 | 2680 | Mpa |
| -- | ISO 527-2/1 | 2680 | Mpa | |
| Tensile strength | Yield 3 | ASTM D638 | 65.0 | Mpa |
| Yield 4 | ASTM D638 | 60.0 | Mpa | |
| Yield | ISO 527-2/5 | 61.0 | Mpa | |
| Yield | ISO 527-2/50 | 66.0 | Mpa | |
| Break 4 | ASTM D638 | 49.0 | Mpa | |
| Break 3 | ASTM D638 | 47.0 | Mpa | |
| Break | ISO 527-2/5 | 46.0 | Mpa | |
| Break | ISO 527-2/50 | 47.0 | Mpa | |
| elongation | Yield 4 | ASTM D638 | 4.0 | % |
| Yield 3 | ASTM D638 | 4.0 | % | |
| Yield | ISO 527-2/5, ISO 527-2/50 | 4.0 | % | |
| Break 4 | ASTM D638 | 58 | % | |
| Break 3 | ASTM D638 | 31 | % | |
| Break | ISO 527-2/5 | 50 | % | |
| Break | ISO 527-2/50 | 21 | % | |
| Bending modulus 5 | ISO 178 | 2720 | Mpa | |
| Bending stress 5, 6 | ISO 178 | 97.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature 8 | 0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span | ISO 75-2/Bf | 90.0 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span | ISO 75-2/Af | 81.0 | °C | |
| Vicat softening temperature | -- | ISO 306/B50 | 96.0 | °C |
| -- | ISO 306/B120 | 98.0 | °C | |
| Linear coefficient of thermal expansion | Flow : -40 to 40°C | ISO 11359-2 | 6.3E-5 | cm/cm/°C |
| Across Flow : -40°C | ISO 11359-2 | 6.3E-5 | cm/cm/°C |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 260°C, 1500 sec^-1 | ISO 11443 | 105 | Pa·s |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 到 90 | °C | ||
| drying time | 2.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Hopper temperature | 60 到 80 | °C | ||
| Temperature at the rear of the barrel | 200 到 230 | °C | ||
| Temperature in the middle of the barrel | 220 到 260 | °C | ||
| Temperature at the front of the material cylinder | 230 到 270 | °C | ||
| Spray nozzle temperature | 220 到 260 | °C | ||
| Processing (melt) temperature | 230 到 270 | °C | ||
| Mold temperature | 50 到 70 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 85.0 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.0 mm, Testing by SABIC | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.