Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ASA XTPMFR10-1000 SABIC INNOVATIVE NANSHA
GELOY™
Electrical applications、Automotive Applications
Thermal stability、Antistatic、High mobility
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PC/ASA/SABIC INNOVATIVE NANSHA/XTPMFR10-1000
Molten Volume Flow Rate (MVR)
260°C/2.16 kg
ISO 1133
cm3/10min
3
Mechanical performance
Test Condition
Test Method
Unit
PC/ASA/SABIC INNOVATIVE NANSHA/XTPMFR10-1000
Tensile strength
屈服 3
ASTM D638
Mpa
6
Tensile strength
屈服 4
ASTM D638
Mpa
6
Tensile strength
屈服
ISO 527-2/5
Mpa
6
Tensile strength
屈服
ISO 527-2/50
Mpa
6
Tensile strength
断裂 4
ASTM D638
Mpa
4
Tensile strength
断裂 3
ASTM D638
Mpa
4
Tensile strength
断裂
ISO 527-2/5
Mpa
4
Tensile strength
断裂
ISO 527-2/50
Mpa
4
Tensile modulus
-- 2
ASTM D638
Mpa
2
Tensile modulus
--
ISO 527-2/1
Mpa
2
elongation
屈服 4
ASTM D638
%
4
elongation
屈服 3
ASTM D638
%
4
elongation
屈服
ISO 527-2/5, ISO 527-2/50
%
4
elongation
断裂 4
ASTM D638
%
5
elongation
断裂 3
ASTM D638
%
3
elongation
断裂
ISO 527-2/5
%
5
elongation
断裂
ISO 527-2/50
%
2
Bending modulus 5
ISO 178
Mpa
2
Bending stress 5, 6
ISO 178
Mpa
9
Thermal performance
Test Condition
Test Method
Unit
PC/ASA/SABIC INNOVATIVE NANSHA/XTPMFR10-1000
Hot deformation temperature 8
0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距
ISO 75-2/Bf
°C
9
Hot deformation temperature 8
1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距
ISO 75-2/Af
°C
8
Vicat softening temperature
--
ISO 306/B50
°C
9
Vicat softening temperature
--
ISO 306/B120
°C
9
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ISO 11359-2
cm/cm/°C
6
Linear coefficient of thermal expansion
横向 : -40°C
ISO 11359-2
cm/cm/°C
6
Filling analysis
Test Condition
Test Method
Unit
PC/ASA/SABIC INNOVATIVE NANSHA/XTPMFR10-1000
Melt viscosity
260°C, 1500 sec^-1
ISO 11443
Pa·s
1
Impact performance
Test Condition
Test Method
Unit
PC/ASA/SABIC INNOVATIVE NANSHA/XTPMFR10-1000
Multi axis Instrumented Impact Energy
ISO 6603-2
J
8