PPA AMODEL® AT-6115HS BK324 SOLVAY USA
129
- Unit Price:
- $7204 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 30MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Thermal stability Filler: Glass fiber reinf 15% filler by weight
- Application Areas:Valves/valve components Industrial components Industrial applications Machine/mechanical compon Metal substitution Connector Parts under the hood of a Vehicle electronics Application in the automo Automotive Applications currency Shell
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | ASTMD955 | 1.0 | % |
| TD | ASTMD955 | 1.1 | % | |
| Water absorption rate | 24hr | ASTMD570 | 0.20 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ASTMD638 | 5380 | Mpa | |
| 23°C | ISO527-2 | 5200 | Mpa | |
| 100°C | ISO527-2 | 3100 | Mpa | |
| Tensile strength | ASTMD638 | 122 | Mpa | |
| Tensile stress | Break,23°C | ISO527-2 | 126 | Mpa |
| compressive strength | ASTMD695 | 100 | Mpa | |
| shear strength | ASTMD732 | 56.5 | Mpa | |
| Tensile stress | Break,24°C | ISO527-2 | 68.3 | Mpa |
| elongation | Break | ASTMD638 | 3.4 | % |
| Tensile strain | Break,23°C | ISO527-2 | 4.1 | % |
| Break,24°C | ISO527-2 | 7.7 | % | |
| Bending modulus | ASTMD790 | 4410 | Mpa | |
| 23°C | ISO178 | 4270 | Mpa | |
| 100°C | ISO178 | 2340 | Mpa | |
| bending strength | ASTMD790 | 165 | Mpa | |
| Bending stress | 23°C | ISO178 | 170 | Mpa |
| 100°C | ISO178 | 66.9 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Annealed | ASTMD648 | 260 | °C |
| Peak melting temperature | ASTMD3418 | 305 | °C | |
| Melting temperature | ISO11357-3 | 305 | °C | |
| Linear coefficient of thermal expansion | MD：0to100°C | ASTME831 | 2.2E-05 | cm/cm/°C |
| MD：100to200°C | ASTME831 | 3E-05 | cm/cm/°C | |
| TD：0to100°C | ASTME831 | 9E-05 | cm/cm/°C | |
| TD：100to200°C | ASTME831 | 1.2E-04 | cm/cm/°C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 298 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 251 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 76 | kJ/m² |
| Unscented Izod impact strength | 23°C | ISO180/1U | 55 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.