PPA AT-6115HS BK324 SOLVAY USA
AMODEL®
Valves/valve components、Industrial components、Industrial applications、Machine/mechanical compon、Metal substitution、Connector、Parts under the hood of a、Vehicle electronics、Application in the automo、Automotive Applications、currency、Shell
High temperature resistan、Thermal stability、Filler: Glass fiber reinf、15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPA/SOLVAY USA/AT-6115HS BK324
Shrinkage rate
MD
ASTMD955
%
1
Shrinkage rate
TD
ASTMD955
%
1
Water absorption rate
24hr
ASTMD570
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPA/SOLVAY USA/AT-6115HS BK324
shear strength
ASTMD732
Mpa
5
Tensile strength
ASTMD638
Mpa
1
Tensile modulus
ASTMD638
Mpa
5
Tensile modulus
23°C
ISO527-2
Mpa
5
Tensile modulus
100°C
ISO527-2
Mpa
3
Tensile strain
断裂,23°C
ISO527-2
%
4
Tensile strain
断裂,24°C
ISO527-2
%
7
Tensile stress
断裂,23°C
ISO527-2
Mpa
1
Tensile stress
断裂,24°C
ISO527-2
Mpa
6
elongation
断裂
ASTMD638
%
3
Bending modulus
ASTMD790
Mpa
4
Bending modulus
23°C
ISO178
Mpa
4
Bending modulus
100°C
ISO178
Mpa
2
bending strength
ASTMD790
Mpa
1
Bending stress
23°C
ISO178
Mpa
1
Bending stress
100°C
ISO178
Mpa
6
compressive strength
ASTMD695
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PPA/SOLVAY USA/AT-6115HS BK324
Hot deformation temperature
1.8MPa,退火
ASTMD648
°C
2
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Peak melting temperature
ASTMD3418
°C
3
Melting temperature
ISO11357-3
°C
3
Linear coefficient of thermal expansion
MD：0to100°C
ASTME831
cm/cm/°C
2
Linear coefficient of thermal expansion
MD：100到200°C
ASTME831
cm/cm/°C
3
Linear coefficient of thermal expansion
TD：0to100°C
ASTME831
cm/cm/°C
9
Linear coefficient of thermal expansion
TD：100到200°C
ASTME831
cm/cm/°C
1
Impact performance
Test Condition
Test Method
Unit
PPA/SOLVAY USA/AT-6115HS BK324
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
7
Unscented Izod impact strength
23°C
ISO180/1U
kJ/m²
5