PPA AMODEL® AT-1002 HS SOLVAY USA
148
- Unit Price:
- $8411 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 34MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High temperature resistan Thermal stability
- Application Areas:Industrial applications Automotive Applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | ASTMD955 | 2.0 | % |
| TD | ASTMD955 | 2.1 | % | |
| Water absorption rate | 24hr | ASTMD570 | 0.50 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Yield,23°C | ISO527-2 | 75.2 | Mpa |
| Yield,100°C | ISO527-2 | 38.6 | Mpa | |
| Break,23°C | ISO527-2 | 68.3 | Mpa | |
| Tensile strain | Yield,23°C | ISO527-2 | 5.0 | % |
| Yield,100°C | ISO527-2 | 3.7 | % | |
| Break,23°C | ISO527-2 | 15 | % | |
| Tensile modulus | ASTMD638 | 2760 | Mpa | |
| 23°C | ISO527-2 | 2760 | Mpa | |
| 100°C | ISO527-2 | 2100 | Mpa | |
| Bending modulus | ASTMD790 | 2210 | Mpa | |
| 23°C | ISO178 | 2280 | Mpa | |
| 100°C | ISO178 | 1720 | Mpa | |
| bending strength | ASTMD790 | 103 | Mpa | |
| Bending stress | 23°C | ISO178 | 79.3 | Mpa |
| 100°C | ISO178 | 49.6 | Mpa | |
| Tensile strength | ASTMD638 | 83.4 | Mpa | |
| shear strength | ASTMD732 | 64.1 | Mpa | |
| Elongation rate 2 | Break | ASTMD638 | 80 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Peak melting temperature | ASTMD3418 | 315 | °C | |
| Linear coefficient of thermal expansion | MD：100to200°C | ASTME831 | 1.3E-04 | cm/cm/°C |
| TD：0to100°C | ASTME831 | 9.3E-05 | cm/cm/°C | |
| TD：100to200°C | ASTME831 | 1.4E-04 | cm/cm/°C | |
| MD：0to100°C | ASTME831 | 7.8E-05 | cm/cm/°C | |
| Melting temperature | ISO11357-3 | 315 | °C | |
| Hot deformation temperature | 0.45MPa,Annealed | ASTMD648 | 163 | °C |
| 1.8MPa,Unannealed | ISO75-2/Af | 118 | °C | |
| 1.8MPa,Annealed | ASTMD648 | 121 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | 8E+13 | ohms | |
| Dielectric constant | 60Hz | ASTMD150 | 3.30 | |
| 1MHz | ASTMD150 | 3.30 | ||
| Volume resistivity | ASTMD257 | 1.2E+16 | ohms·cm | |
| Dielectric strength | ASTMD149 | 17 | KV/mm | |
| Dissipation factor | 60Hz | ASTMD150 | 4E-03 | |
| 1MHz | ASTMD150 | 0.016 | ||
| Leakage Trace Index | ASTMD3638 | >600 | V | |
| High voltage arc tracing rate | HVTR | UL746 | 12.0 | mm/min |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| PenetrationImpact3 | ASTMD3763 | 4448 | N | |
| Dart impact equipped with measuring instruments | TotalEnergy | ASTMD3763 | 54.2 | J |
| Unscented Izod impact strength | 23°C | ISO180/1U | NoBreak | |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | NoBreak |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating 5 | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.