PEI ULTEM™ Resin AUT200AR BK1E157S SABIC INNOVATIVE SPAIN
138
- Unit Price:
- $16596 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt flow rate | 337°C/6.7 kg | ASTM D1238 | 18 | g/10 min |
| Molten Volume Flow Rate (MVR) | 360°C/5.0 kg | ISO 1133 | 25.0 | cm3/10min |
| Shrinkage rate | Flow : 3.20 mm | 内部方法 | 0.50 到 0.70 | % |
| Across Flow : 3.20 mm | 内部方法 | 0.50 到 0.70 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 1.3 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 3200 | Mpa | |
| Tensile stress | Yield | ISO 527-2/5 | 105 | Mpa |
| Break | ISO 527-2/5 | 85.0 | Mpa | |
| Tensile strain | Yield | ISO 527-2/5 | 6.0 | % |
| Break | ISO 527-2/5 | 60 | % | |
| Bending modulus 1 | ISO 178 | 3300 | Mpa | |
| Bending stress 1, 2 | ISO 178 | 160 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 5 | ISO 75-2/Be | 200 | °C |
| 1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 5 | ISO 75-2/Ae | 190 | °C | |
| 1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 4 | ISO 75-2/Af | 193 | °C | |
| Vicat softening temperature | -- | ISO 306/A50 | 215 | °C |
| -- | ISO 306/B50 | 211 | °C | |
| -- | ISO 306/B120 | 212 | °C | |
| Linear coefficient of thermal expansion | Flow : 23 to 150°C | ISO 11359-2 | 5.0E-5 | cm/cm/°C |
| Across Flow : 23 to 150°C | ISO 11359-2 | 5.0E-5 | cm/cm/°C |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 150 | °C | ||
| drying time | 4.0 到 6.0 | hr | ||
| Suggested maximum moisture content | 0.020 | % | ||
| Suggested injection volume | 40 到 60 | % | ||
| Temperature at the rear of the barrel | 330 到 400 | °C | ||
| Temperature in the middle of the barrel | 340 到 400 | °C | ||
| Temperature at the front of the material cylinder | 345 到 400 | °C | ||
| Spray nozzle temperature | 345 到 400 | °C | ||
| Processing (melt) temperature | 350 到 400 | °C | ||
| Mold temperature | 135 到 165 | °C | ||
| Back pressure | 0.300 到 0.700 | Mpa | ||
| Screw speed | 40 到 70 | rpm | ||
| Exhaust hole depth | 0.025 到 0.076 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Suspended wall beam gap impact strength 4 | -30°C | ISO 180/1A | 5.0 | kJ/m² |
| 23°C | ISO 180/1A | 5.0 | kJ/m² | |
| Unscented Izod Impact Strength 4 | -30°C | ISO 180/1U | 无断裂 | |
| 23°C | ISO 180/1U | 无断裂 | ||
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 33.0 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FMVSS Burning Speed | 2.00 mm | FMVSS 302 | 0 到 5 | mm/min |
| Metallized Haze Onset | 内部方法 | 204 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.