Melt flow rate

337°C/6.7 kg

ASTM D1238

g/10 min

1

Molten Volume Flow Rate (MVR)

360°C/5.0 kg

ISO 1133

cm3/10min

2

Shrinkage rate

流动 : 3.20 mm

内部方法

%

0

Shrinkage rate

横向流动 : 3.20 mm

内部方法

%

0

Water absorption rate

饱和, 23°C

ISO 62

%

1

Water absorption rate

平衡, 23°C, 50% RH

ISO 62

%

0

Tensile modulus

ISO 527-2/1

Mpa

3

Tensile strain

屈服

ISO 527-2/5

%

6

Tensile strain

断裂

ISO 527-2/5

%

6

Tensile stress

屈服

ISO 527-2/5

Mpa

1

Tensile stress

断裂

ISO 527-2/5

Mpa

8

Bending modulus 1

ISO 178

Mpa

3

Bending stress 1, 2

ISO 178

Mpa

1

Hot deformation temperature

0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 5

ISO 75-2/Be

°C

2

Hot deformation temperature

1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 5

ISO 75-2/Ae

°C

1

Hot deformation temperature

1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 4

ISO 75-2/Af

°C

1

Vicat softening temperature

--

ISO 306/A50

°C

2

Vicat softening temperature

--

ISO 306/B50

°C

2

Vicat softening temperature

--

ISO 306/B120

°C

2

Linear coefficient of thermal expansion

流动 : 23 到 150°C

ISO 11359-2

cm/cm/°C

5

Linear coefficient of thermal expansion

横向 : 23 到 150°C

ISO 11359-2

cm/cm/°C

5

Suspended wall beam gap impact strength 4

-30°C

ISO 180/1A

kJ/m²

5

Suspended wall beam gap impact strength 4

23°C

ISO 180/1A

kJ/m²

5

Dart impact equipped with measuring instruments

23°C, Total Energy

ASTM D3763

J

3

FMVSS Burning Speed

2.00 mm

FMVSS 302

mm/min

0

Metallized Haze Onset

内部方法

°C

2