PBT NOVADURAN™ 5820G30 M MITSUBISHI ENGINEERING JAPAN
141
- Unit Price:
- $4247 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:high strength
- Application Areas:Electronic and Electrical Automotive sector
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Molten Volume Flow Rate (MVR) | 250°C/5.0 kg | ISO 1133 | 24.0 | cm3/10min |
| Shrinkage rate | Across Flow : 2.00 mm | 内部方法 | 0.70 | % |
| 流量 : 2.00 mm | 内部方法 | 0.30 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.070 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 10600 | Mpa | |
| Tensile stress | Break | ISO 527-2/5 | 134 | Mpa |
| Tensile strain | Break | ISO 527-2/5 | 2.0 | % |
| Bending modulus 2 | ISO 178 | 9900 | Mpa | |
| Bending stress 2 | ISO 178 | 190 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Annealed | ISO 75-2/B | 212 | °C |
| 1.8 MPa, Annealed | ISO 75-2/A | 178 | °C | |
| Melting temperature | ISO 11357-3 | 224 | °C | |
| Linear coefficient of thermal expansion | Flow : -30 to 35°C | ISO 11359-2 | 2.0E-5 | cm/cm/°C |
| Flow : -30 to 120°C | ISO 11359-2 | 2.0E-5 | cm/cm/°C | |
| Flow : 35 to 120°C | ISO 11359-2 | 2.0E-5 | cm/cm/°C | |
| Across Flow : -30 to 35°C | ISO 11359-2 | 8.0E-5 | cm/cm/°C | |
| Across Flow : -30 to 120°C | ISO 11359-2 | 1.1E-4 | cm/cm/°C | |
| Across Flow : 35 to 120°C | ISO 11359-2 | 1.4E-4 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | 6.0E+15 | ohms | |
| Volume resistivity | IEC 60093 | 1.0E+14 | ohms·cm | |
| Dielectric strength | 1.00 mm | IEC 60243-1 | 33 | KV/mm |
| 2.00 mm | IEC 60243-1 | 30 | KV/mm | |
| Dielectric constant | 1 MHz | IEC 60250 | 3.30 | |
| Dissipation factor | 1 MHz | IEC 60250 | 0.017 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Temperature - Vacuum Drying Machine | 120 | °C | ||
| Drying time - vacuum dryer | 5.0 到 8.0 | hr | ||
| Temperature at the rear of the barrel | 240 | °C | ||
| Temperature in the middle of the barrel | 245 | °C | ||
| Temperature at the front of the material cylinder | 255 | °C | ||
| Spray nozzle temperature | 255 | °C | ||
| Mold temperature | 80 到 100 | °C | ||
| Injection pressure | 20.0 到 150 | Mpa | ||
| Injection speed | 中等偏快 | |||
| Screw speed | 80 到 120 | rpm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 38 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.