PBT 5820G30 M MITSUBISHI ENGINEERING JAPAN
NOVADURAN™
Electronic and Electrical、Automotive sector
high strength
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/MITSUBISHI ENGINEERING JAPAN/5820G30 M
Molten Volume Flow Rate (MVR)
250°C/5.0 kg
ISO 1133
cm3/10min
2
Shrinkage rate
横向流量 : 2.00 mm
内部方法
%
0
Shrinkage rate
流量 : 2.00 mm
内部方法
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/MITSUBISHI ENGINEERING JAPAN/5820G30 M
Tensile modulus
ISO 527-2/1
Mpa
1
Tensile strain
断裂
ISO 527-2/5
%
2
Tensile stress
断裂
ISO 527-2/5
Mpa
1
Bending modulus 2
ISO 178
Mpa
9
Bending stress 2
ISO 178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PBT/MITSUBISHI ENGINEERING JAPAN/5820G30 M
Hot deformation temperature
0.45 MPa, 退火
ISO 75-2/B
°C
2
Hot deformation temperature
1.8 MPa, 退火
ISO 75-2/A
°C
1
Melting temperature
ISO 11357-3
°C
2
Linear coefficient of thermal expansion
流动 : -30 到 35°C
ISO 11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
流动 : -30 到 120°C
ISO 11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
流动 : 35 到 120°C
ISO 11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
横向 : -30 到 35°C
ISO 11359-2
cm/cm/°C
8
Linear coefficient of thermal expansion
横向 : -30 到 120°C
ISO 11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
横向 : 35 到 120°C
ISO 11359-2
cm/cm/°C
1
Electrical performance
Test Condition
Test Method
Unit
PBT/MITSUBISHI ENGINEERING JAPAN/5820G30 M
Surface resistivity
IEC 60093
ohms
6
Dielectric strength
1.00 mm
IEC 60243-1
KV/mm
3
Dielectric strength
2.00 mm
IEC 60243-1
KV/mm
3
Volume resistivity
IEC 60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PBT/MITSUBISHI ENGINEERING JAPAN/5820G30 M
Impact strength of simply supported beam without notch
23°C
ISO 179
kJ/m²
3