PBT VALOX™ 420HP-1001 SABIC INNOVATIVE NANSHA
138
Unit Price:$5330 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced dimensional stability High rigidity high strength heat-resisting
- Application Areas:Lawn equipment Electrical field Electrical appliances Electronic field Plastic bag Engine hood parts Textile application Industrial applications Nursing supplies Household goods Architectural application Automotive interior parts Automotive External Parts Petroleum Applications Outdoor applications sporting goods Natural gas supplies Medical supplies Garden equipment Casters Lighting applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Specific volume | ASTMD792 | 0.650 | cm³/g | |
| Melt mass flow rate | 250°C/2.16kg | ASTMD1238 | 17 | g/10min |
| Melt volume flow rate | 250°C/2.16kg | ISO1133 | 13.0 | cm3/10min |
| Shrinkage rate | TD：--3 | 内部方法 | 0.40to0.60 | % |
| TD：--4 | 内部方法 | 0.50to1.0 | % | |
| TD：3.20mm | 内部方法 | 0.50to1.0 | % | |
| Water absorption rate | 24hr | ASTMD570 | 0.060 | % |
| Saturation,23°C | ISO62 | 0.26 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 0.080 | % | |
| Shrinkage rate | MD：--2 | 内部方法 | 0.50to0.80 | % |
| MD：--3 | 内部方法 | 0.30to0.50 | % | |
| MD：--4 | 内部方法 | 0.30to0.70 | % | |
| MD：3.20mm | 内部方法 | 0.30to0.80 | % | |
| TD：--5 | 内部方法 | 0.60to0.90 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 6 | ASTMD638 | 9300 | Mpa | |
| Tensile modulus | ISO527-2/1 | 9300 | Mpa | |
| Tensile strength 7 | Yield | ASTMD638 | 120 | Mpa |
| Tensile stress | Yield | ISO527-2/5 | 125 | Mpa |
| Tensile strength 7 | Break | ASTMD638 | 120 | Mpa |
| Tensile stress | Break | ISO527-2/5 | 125 | Mpa |
| Tensile strain 7 | Yield | ASTMD638 | 3.0 | % |
| Tensile strain | Yield | ISO527-2/5 | 2.0 | % |
| Tensile strain 7 | Break | ASTMD638 | 3.0 | % |
| Tensile strain | Break | ISO527-2/5 | 2.0 | % |
| Bending modulus 8 | 50.0mmSpan | ASTMD790 | 7580 | Mpa |
| Bending modulus 9 | ISO178 | 8500 | Mpa | |
| Bending strength 9,10 | ISO178 | 195 | Mpa | |
| Flexural Strength8 | Break,50.0mmSpan | ASTMD790 | 189 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,3.20mm | ASTMD648 | 220 | °C |
| 0.45MPa,Unannealed,6.40mm | ASTMD648 | 216 | °C | |
| Hot deformation temperature 13 | 0.45MPa,Unannealed,64.0mmSpan | ISO75-2/Bf | 217 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 203 | °C |
| Hot deformation temperature 13 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 204 | °C |
| Vicat softening temperature | ASTMD152514 | 215 | °C | |
| -- | ISO306/A50 | 223 | °C | |
| -- | ISO306/B50 | 215 | °C | |
| -- | ISO306/B120 | 215 | °C | |
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 2.5E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 2.5E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 1.2E-04 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 1.2E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ASTMD257 | >3.2E+16 | ohms·cm | |
| Dielectric strength | 1.60mm,in Oil | ASTMD149 | 25 | KV/mm |
| 3.20mm,inAir | ASTMD149 | 19 | KV/mm | |
| Dielectric constant | 100Hz | ASTMD150 | 3.80 | |
| 1MHz | ASTMD150 | 3.70 | ||
| Dissipation factor | 100Hz | ASTMD150 | 2E-03 | |
| 1MHz | ASTMD150 | 0.020 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 11 | -30°C | ISO179/1eA | 5.0 | kJ/m² |
| 23°C | ISO179/1eA | 5.0 | kJ/m² | |
| Simply supported beam without notch impact strength 11 | -30°C | ISO179/1eU | 45 | kJ/m² |
| 23°C | ISO179/1eU | 45 | kJ/m² | |
| Suspended wall beam gap impact strength 12 | -30°C | ISO180/1A | 7.0 | kJ/m² |
| 23°C | ISO180/1A | 8.0 | kJ/m² | |
| Unscented Izod Impact Strength 12 | -30°C | ISO180/1U | 45 | kJ/m² |
| 23°C | ISO180/1U | 45 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 8.00 | J |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Scale | ASTMD785 | 118 |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Filling material | ASTMD229 | 30 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.