Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 420HP-1001 SABIC INNOVATIVE NANSHA
VALOX™
Lawn equipment、Electrical field、Electrical appliances、Electronic field、Plastic bag、Engine hood parts、Textile application、Industrial applications、Nursing supplies、Household goods、Architectural application、Automotive interior parts、Automotive External Parts、Petroleum Applications、Outdoor applications、sporting goods、Natural gas supplies、Medical supplies、Garden equipment、Casters、Lighting applications
Glass fiber reinforced、dimensional stability 、High rigidity、high strength、heat-resisting
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/420HP-1001
Melt volume flow rate
250°C/2.16kg
ISO1133
cm3/10min
1
Melt mass flow rate
250°C/2.16kg
ASTMD1238
g/10min
1
Shrinkage rate
TD：--3
内部方法
%
0
Shrinkage rate
TD：--4
内部方法
%
0
Shrinkage rate
TD：3.20mm
内部方法
%
0
Shrinkage rate
MD：--2
内部方法
%
0
Shrinkage rate
MD：--3
内部方法
%
0
Shrinkage rate
MD：--4
内部方法
%
0
Shrinkage rate
MD：3.20mm
内部方法
%
0
Shrinkage rate
TD：--5
内部方法
%
0
Specific volume
ASTMD792
cm³/g
0
Water absorption rate
24hr
ASTMD570
%
0
Water absorption rate
饱和,23°C
ISO62
%
0
Water absorption rate
平衡,23°C,50%RH
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/420HP-1001
Flexural Strength8
Break,50.0mmSpan
ASTMD790
Mpa
1
Tensile modulus
ISO527-2/1
Mpa
9
Tensile modulus 6
ASTMD638
Mpa
9
Tensile strength 7
Yield
ASTMD638
Mpa
1
Tensile strength 7
Break
ASTMD638
Mpa
1
Tensile strain
屈服
ISO527-2/5
%
2
Tensile strain
断裂
ISO527-2/5
%
2
Tensile strain 7
Break
ASTMD638
%
3
Tensile strain 7
Yield
ASTMD638
%
3
Tensile stress
断裂
ISO527-2/5
Mpa
1
Tensile stress
屈服
ISO527-2/5
Mpa
1
Bending modulus 8
50.0mmSpan
ASTMD790
Mpa
7
Bending modulus 9
ISO178
Mpa
8
Bending strength 9,10
ISO178
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/420HP-1001
Hot deformation temperature
0.45MPa,未退火,3.20mm
ASTMD648
°C
2
Hot deformation temperature
0.45MPa,未退火,6.40mm
ASTMD648
°C
2
Hot deformation temperature
1.8MPa,未退火,3.20mm
ASTMD648
°C
2
Hot deformation temperature 13
1.8MPa,Unannealed,64.0mmSpan
ISO75-2/Af
°C
2
Hot deformation temperature 13
0.45MPa,Unannealed,64.0mmSpan
ISO75-2/Bf
°C
2
Vicat softening temperature
ASTMD152514
°C
2
Vicat softening temperature
--
ISO306/A50
°C
2
Vicat softening temperature
--
ISO306/B50
°C
2
Vicat softening temperature
--
ISO306/B120
°C
2
Linear coefficient of thermal expansion
MD：-40到40°C
ASTME831
cm/cm/°C
2
Linear coefficient of thermal expansion
MD：-40到40°C
ISO11359-2
cm/cm/°C
2
Linear coefficient of thermal expansion
TD：-40到40°C
ASTME831
cm/cm/°C
1
Linear coefficient of thermal expansion
TD：-40到40°C
ISO11359-2
cm/cm/°C
1
Electrical performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/420HP-1001
Dielectric strength
1.60mm,在油中
ASTMD149
KV/mm
2
Dielectric strength
3.20mm,inAir
ASTMD149
KV/mm
1
Volume resistivity
ASTMD257
ohms·cm
>
Impact performance
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/420HP-1001
Impact strength of simply supported beam gap 11
-30°C
ISO179/1eA
kJ/m²
5
Impact strength of simply supported beam gap 11
23°C
ISO179/1eA
kJ/m²
5
Simply supported beam without notch impact strength 11
-30°C
ISO179/1eU
kJ/m²
4
Simply supported beam without notch impact strength 11
23°C
ISO179/1eU
kJ/m²
4
Unscented Izod Impact Strength 12
-30°C
ISO180/1U
kJ/m²
4
Unscented Izod Impact Strength 12
23°C
ISO180/1U
kJ/m²
4
Suspended wall beam gap impact strength 12
-30°C
ISO180/1A
kJ/m²
7
Suspended wall beam gap impact strength 12
23°C
ISO180/1A
kJ/m²
8
Dart impact equipped with measuring instruments
23°C,TotalEnergy
ASTMD3763
J
8
Supplementary Information
Test Condition
Test Method
Unit
PBT/SABIC INNOVATIVE NANSHA/420HP-1001
Filling material
ASTMD229
%
3