PBT Ultradur® B4300K6 BASF GERMANY
128
- Unit Price:
- $3753 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity Glass fiber reinforced
- Application Areas:electrical machinery Engineering accessories Shell printed circuit board
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Apparent density | 0.70 到 0.80 | g/cm³ | ||
| Melt volume flow rate | 250℃，2.16 kg 250℃/2.16 kg | ISO 1133 | 9 | cm3/10min |
| Stickiness number | ISO 307 | 113 | cm³/g | |
| Water absorption rate | Saturation，23℃ Saturation, 73°F | ISO 62 | 0.4 | % |
| Equilibrium，23℃，50% RH Equilibrium, 73°F, 50% RH | ISO 62 | 0.2 | % | |
| Shrinkage rate | MD：自由的 free, longitudinal | 1.7 | % | |
| TD：自由的 free, transverse | 1.7 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | Break Break | ISO 527-2 | 50 | Mpa |
| Tensile modulus | ISO 527-2 | 4000 | Mpa | |
| Tensile strain | Break Break | ISO 527-2 | 5 | % |
| Tensile creep modulus | 1000 hr 1000 hr 5 | ISO 899-1 | 2200 | Mpa |
| Ball pressure hardness | H358/30 | ISO 2039-1 | 165 | Mpa |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Relative permittivity | 100 Hz 100 Hz | IEC 60250 | 3.8 | |
| 1 MHz 1 MHz | IEC 60250 | 3.8 | ||
| Dissipation factor | 100 Hz 100 Hz | IEC 60250 | 0.0012 | |
| 1 MHz 1 MHz | IEC 60250 | 0.019 | ||
| Compared to the leakage trace index | Solution A Solution A | IEC 60112 | 225 | V |
| Solution B Solution B | IEC 60112 | 150 | V | |
| Volume resistivity | IEC 60093 | 10000000000000000 | ohms·cm | |
| Surface resistivity | IEC 60093 | 10000000000000 | ohms |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C -30°C | ISO 179/1eU | 24 | kJ/m² |
| 23℃ 23°C | ISO 179/1eU | 35 | kJ/m² |
| Special Value | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flammability level | 0.75 mm 0.75 mm | HB | ||
| 1.6 mm 1.6 mm | HB |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature | ISO 11357-3 | 223 | °C | |
| Linear coefficient of thermal expansion | MD：23~80℃ MD：23 to 80℃ | ISO 11359-2 | 7.0E-5 到 8.0E-5 | 1/℃ |
| Specific heat | 1500 | J/kg/℃ | ||
| thermal conductivity | DIN 52612 | 0.27 | W/m/K | |
| Temperature index - at 50% loss of tensile strength | -- -- 6 6 | IEC 60216 | 120 | °C |
| Temperature index - at 51% loss of tensile strength | -- -- 7 7 | IEC 60216 | 130 | °C |
| Maximum operating temperature | short cycle operation | 200 | °C | |
| Hot deformation temperature | 0.45 MPa，Unannealed 66 psi, Unannealed | ISO 75-2/B | 200 | °C |
| 1.8 MPa，Unannealed 264 psi, Unannealed | ISO 75-2/A | 95 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.