Melt volume flow rate

250℃，2.16 kg  250℃/2.16 kg

ISO 1133

cm3/10min

9

Water absorption rate

饱和，23℃  Saturation, 73°F

ISO 62

%

0

Water absorption rate

平衡，23℃，50% RH  Equilibrium, 73°F, 50% RH

ISO 62

%

0

Stickiness number

ISO 307

cm³/g

1

Tensile modulus

ISO 527-2

Mpa

4

tensile strength

断裂  断裂

ISO 527-2

Mpa

5

Tensile creep modulus

1000 hr  1000 hr 5

ISO 899-1

Mpa

2

Tensile strain

断裂  断裂

ISO 527-2

%

5

Ball pressure hardness

H358/30  

ISO 2039-1

Mpa

1

Impact strength of simply supported beam without notch

 -30°C -30°C

ISO 179/1eU

kJ/m²

2

Impact strength of simply supported beam without notch

23℃  23°C

ISO 179/1eU

kJ/m²

3

thermal conductivity

DIN 52612

W/m/K

0

Hot deformation temperature

0.45 MPa，未退火  66 psi, Unannealed

ISO 75-2/B

°C

2

Hot deformation temperature

1.8 MPa，未退火  264 psi, Unannealed

ISO 75-2/A

°C

9

Melting temperature

ISO 11357-3

°C

2

Temperature index - at 50% loss of tensile strength

--  --   6 6

IEC 60216

°C

1

Temperature index - at 51% loss of tensile strength

--  --   7 7

IEC 60216

°C

1

Linear coefficient of thermal expansion

MD：23~80℃  MD：23 到 80℃

ISO 11359-2

1/℃

7

Surface resistivity

IEC 60093

ohms

1

Volume resistivity

IEC 60093

ohms·cm

1

Compared to the leakage trace index

解决方案 A  Solution A

IEC 60112

V

2

Compared to the leakage trace index

解决方案 B  Solution B

IEC 60112

V

1