PBT Toraycon® 1401X06 TORAY JAPAN

195

Unit Price:
$4038 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
13MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Flame retardant
Application Areas:Automotive sector Shell
Color:--
Grade:Injection grade

Technical Data Sheet Compare

Physical properties	Test Condition	Test Method	Test Result	Unit
density		ASTM D792/ISO 1183	1.31
Water absorption rate 23 ℃/24h		ASTM D570/ISO 62	0.08	%

physical property	Test Condition	Test Method	Test Result	Unit
Taber wear amount	1.000g·CS-17	ASTM D-1044	10	毫克/1.000m
Film plastic shrinkage	80×80×3板材		1.7-2.3	%
Coefficient of friction	金属	ASTM D-1894	0.13
Coefficient of friction	Coefficient of friction	本身	ASTM D-1894	0.17
Under load	4.6kg/cm	ASTM D-648	154	°C
Under load	Under load	18.6kg/cm	ASTM D-648	58	°C
Shrinkage rate	TD:3.00mm2	内部方法	2.3	%
Shrinkage rate	Shrinkage rate	MD:3.00mm4	内部方法	1.7	%
Water absorption rate	23°C,24hr	ISO62	0.080	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	23°C	ISO527-2	2700	Mpa
Tensile stress	Yield,23°C	ISO527-2	55.0	Mpa
Tensile strain	Break,23°C	ISO527-2	30	%
Bending modulus	23°C	ISO178	2500	Mpa
Bending stress	23°C	ISO178	90.0	Mpa
Friction coefficient 4			0.17
Friction coefficient vs. Metal5		SuzukiMethod	0.13
compressive strength	23℃	ASTM D-695	900	kg/cm
bending strength	23℃	ASTM D-790	900	kg/cm
tensile strength	23℃	ASTM D-638	600	kg/cm
Bending modulus	23℃	ASTM D-790	26	kg/cm
Rockwell hardness		ASTM D-785	75	M标度
Fracture tensile elongation	23℃	ASTM D-638	15	%
elongation at break		ASTM D638/ISO 527	100	%
tensile strength		ASTM D638/ISO 527	55	kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	M75
Bending modulus		ASTM D790/ISO 178	2.5	kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	85	kg/cm²(MPa)[Lb/in²]
IZOD notch impact strength		ASTM D256/ISO 179	45	kg·cm/cm(J/M)ft·lb/in
	IZOD notch impact strength		ASTM D256/ISO 179	35	kg·cm/cm(J/M)ft·lb/in
		IZOD notch impact strength		ASTM D256/ISO 179	nb	kg·cm/cm(J/M)ft·lb/in
		IZOD notch impact strength	IZOD notch impact strength		ASTM D256/ISO 179	120	kg·cm/cm(J/M)ft·lb/in
IZOD impact strength	Unnotched，23℃	ASTM D-256	不破裂	kg·cm/cm
	IZOD impact strength	Unnotched，-40℃	ASTM D-256	120	kg·cm/cm
		IZOD impact strength	Notched，23℃	ASTM D-256	4.4	kg·cm/cm
		IZOD impact strength	IZOD impact strength	Notched，-40℃	ASTM D-256	3.5	kg·cm/cm

Thermal performance	Test Condition	Test Method	Test Result	Unit
Combustibility (rate)		UL94	HB
Hot deformation temperature		ASTM D648/ISO 75	60 1.8Mpa	℃（℉）
Linear expansion coefficient		ASTM D696/ISO 11359	9.4*10^-5	mm/mm.℃
Linear thermal expansion		ASTM D-696	9.4	cm/cm℃×10
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	150	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	60.0	°C
Linear coefficient of thermal expansion	MD：-30to100°C	ISO11359-2	1.1E-04	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity		IEC60093	8E+16	ohms·cm
Dielectric strength		IEC60243-1	17	KV/mm
Dielectric constant 5	23°C,50Hz	IEC60250	3.30
Dielectric constant 5	Dielectric constant 5	23°C,1kHz	IEC60250	3.30
Dissipation factor 6	23°C,50Hz	IEC60250	2E-03
Dissipation factor 6	Dissipation factor 6	23°C,1MHz	IEC60250	0.020
Arc resistance 7		IEC60950	144	sec
Compared to the anti leakage trace index	CTI	UL746	PLC0
Dielectric constant		ASTM D150/IEC 60250	3.3
Volume resistivity		ASTM D257/IEC 60093	4.0*10^14	Ω.cm
Volume resistivity	Volume resistivity		ASTM D-257	4.0	cm×10
Dielectric strength	短时·23℃·1/8时	ASTM D-149	17	KV/mm
Arc resistance		ASTM D-495	144	秒

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-40°C	ISO179	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179	240	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	M-Sale,23°C	ISO2039-2	77

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.8mm	UL94	HB

Basic performance	Test Condition	Test Method	Test Result	Unit
Water absorption rate	23℃·24hr	ASTM D-570	0.08	%

Supplementary Information	Test Condition	Test Method	Test Result	Unit
BarFlowLength8	250°C,1.00mm	内部方法	103	mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.