Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 1401X06 TORAY JAPAN
Toraycon®
Automotive sector、Shell
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Physical properties
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1401X06
Water absorption rate 23 ℃/24h
ASTM D570/ISO 62
%
0
physical property
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1401X06
Under load
4.6kg/cm
ASTM D-648
°C
1
Under load
18.6kg/cm
ASTM D-648
°C
5
Shrinkage rate
TD:3.00mm2
内部方法
%
2
Shrinkage rate
MD:3.00mm4
内部方法
%
1
Taber wear amount
1.000g·CS-17
ASTM D-1044
毫克/1.000m
1
Water absorption rate
23°C,24hr
ISO62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1401X06
Fracture tensile elongation
23℃
ASTM D-638
%
1
elongation at break
ASTM D638/ISO 527
%
1
Tensile modulus
23°C
ISO527-2
Mpa
2
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
5
tensile strength
23℃
ASTM D-638
kg/cm
6
Tensile strain
断裂,23°C
ISO527-2
%
3
Tensile stress
屈服,23°C
ISO527-2
Mpa
5
Rockwell hardness
ASTM D-785
M标度
7
Bending modulus
23°C
ISO178
Mpa
2
Bending modulus
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
2
Bending modulus
23℃
ASTM D-790
kg/cm
2
bending strength
23℃
ASTM D-790
kg/cm
9
bending strength
ASTM D790/ISO 178
kg/cm²(MPa)[Lb/in²]
8
Bending stress
23°C
ISO178
Mpa
9
compressive strength
23℃
ASTM D-695
kg/cm
9
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
4
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
3
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
n
IZOD notch impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
1
IZOD impact strength
无缺口，23℃
ASTM D-256
kg·cm/cm
不
IZOD impact strength
无缺口，-40℃
ASTM D-256
kg·cm/cm
1
IZOD impact strength
缺口，23℃
ASTM D-256
kg·cm/cm
4
IZOD impact strength
缺口，-40℃
ASTM D-256
kg·cm/cm
3
Thermal performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1401X06
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
6
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
1
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
6
Linear coefficient of thermal expansion
MD：-30到100°C
ISO11359-2
cm/cm/°C
1
Linear expansion coefficient
ASTM D696/ISO 11359
mm/mm.℃
9
Linear thermal expansion
ASTM D-696
cm/cm℃×10
9
Electrical performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1401X06
Dielectric strength
IEC60243-1
KV/mm
1
Dielectric strength
短时·23℃·1/8时
ASTM D-149
KV/mm
1
Arc resistance
ASTM D-495
秒
1
Arc resistance 7
IEC60950
sec
1
Volume resistivity
IEC60093
ohms·cm
8
Volume resistivity
ASTM D-257
cm×10
4
Volume resistivity
ASTM D257/IEC 60093
Ω.cm
4
Impact performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1401X06
Impact strength of simply supported beam without notch
23°C
ISO179
kJ/m²
2
Basic performance
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1401X06
Water absorption rate
23℃·24小时
ASTM D-570
%
0
Supplementary Information
Test Condition
Test Method
Unit
PBT/TORAY JAPAN/1401X06
BarFlowLength8
250°C,1.00mm
内部方法
mm
1