Material Description

Technical Data Sheet

Material Description

Material Properties:High temperature resistan High mobility Glass fiber reinforced
Application Areas:Electrical applications Automotive interior parts
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Melt flow rate	280°C/5.0 kg	ASTM D1238	3.5	g/10 min
Molten Volume Flow Rate (MVR)	300°C/5.0 kg	ISO 1133	10.0	cm3/10min
Shrinkage rate - flow	-- 2	内部方法	0.50 到 0.70	%
Shrinkage rate - flow	Shrinkage rate - flow	3.20 mm	内部方法	0.50 到 0.70	%
Water absorption rate	Saturation, 23°C	ISO 62	0.18	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	0.060	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	-- 3	ASTM D638	2500	Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/1	2500	Mpa
Tensile strength	Yield 4	ASTM D638	70.0	Mpa
	Tensile strength	Yield	ISO 527-2/50	70.0	Mpa
		Tensile strength	Break 4	ASTM D638	60.0	Mpa
		Tensile strength	Tensile strength	Break	ISO 527-2/50	55.0	Mpa
elongation	Yield 4	ASTM D638	5.0	%
	elongation	Yield	ISO 527-2/50	4.0	%
		elongation	Break 4	ASTM D638	7.0	%
		elongation	elongation	Break	ISO 527-2/50	10	%
Bending modulus	50.0 mm Span 5	ASTM D790	2550	Mpa
Bending modulus	Bending modulus	-- 6	ISO 178	2400	Mpa
Bending stress	-- 6, 7	ISO 178	110	Mpa
Bending stress	Bending stress	Yield, 50.0 mm Span 5	ASTM D790	105	Mpa
Taber abraser	1000 Cycles, 1000 g, CS-17 Wheel	内部方法	35.0	mg

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm, 100 mm Span 10	ISO 75-2/Be	140	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	135	°C
	Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 100 mm Span 10	ISO 75-2/Ae	130	°C
Vicat softening temperature	--	ASTM D152511, ISO 306/B12011	155	°C
	Vicat softening temperature	--	ISO 306/A50	160	°C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	145	°C
Ball Pressure Test	123 to 127°C	IEC 60695-10-2	通过
Ball Pressure Test	Ball Pressure Test	140°C 12	IEC 60695-10-2	通过
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	7.5E-5	cm/cm/°C
	Linear coefficient of thermal expansion	Flow : 23 to 80°C	ISO 11359-2	7.0E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	7.5E-5	cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 80°C	ISO 11359-2	9.0E-5	cm/cm/°C
thermal conductivity		ISO 8302	0.27	W/m/K
RTI Elec		UL 746	110	°C
RTI Imp		UL 746	105	°C
RTI		UL 746	115	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Surface resistivity		IEC 60093	> 1.0E+15	ohms
Volume resistivity		IEC 60093	1.0E+15	ohms·cm
Dielectric strength	0.800 mm, in Oil	IEC 60243-1	33	KV/mm
	Dielectric strength	1.60 mm, in Oil	IEC 60243-1	26	KV/mm
	Dielectric strength	Dielectric strength	3.20 mm, in Oil	IEC 60243-1	16	KV/mm
Relative permittivity	50 Hz	IEC 60250	2.80
	Relative permittivity	60 Hz	IEC 60250	2.80
	Relative permittivity	Relative permittivity	1 MHz	IEC 60250	2.70
Dissipation factor	50 Hz	IEC 60250	9.0E-4
	Dissipation factor	60 Hz	IEC 60250	9.0E-4
	Dissipation factor	Dissipation factor	1 MHz	IEC 60250	3.0E-3
Leakage Trace Index		IEC 60112	250	V

injection	Test Result	Unit
drying temperature	110 到 120	°C
drying time	2.0 到 3.0	hr
Hopper temperature	80 到 100	°C
Temperature at the rear of the barrel	260 到 280	°C
Temperature in the middle of the barrel	280 到 300	°C
Temperature at the front of the material cylinder	300 到 320	°C
Spray nozzle temperature	280 到 300	°C
Processing (melt) temperature	300 到 320	°C
Mold temperature	100 到 130	°C

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam gap 8	-30°C	ISO 179/1eA	5.0	kJ/m²
Impact strength of simply supported beam gap 8	Impact strength of simply supported beam gap 8	23°C	ISO 179/1eA	14	kJ/m²
Dart impact equipped with measuring instruments	23°C, Total Energy	ASTM D3763	50.0	J

hardness	Test Condition	Test Method	Test Result	Unit
Ball pressure hardness	H 358/30	ISO 2039-1	113	Mpa

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	1.5 mm	UL 94	V-0
UL flame retardant rating	UL flame retardant rating	2.0 mm	UL 94	5VA
Burning wire flammability index	1.0 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	1.0 mm	IEC 60695-2-13	775	°C
	Hot filament ignition temperature	2.0 mm	IEC 60695-2-13	775	°C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	775	°C
Extreme Oxygen Index		ISO 4589-2	32	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.