Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO V0150B-701 SABIC INNOVATIVE SHANGHAI
NORYL™
Electrical applications、Automotive interior parts
High temperature resistan、High mobility、Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/V0150B-701
Melt flow rate
280°C/5.0 kg
ASTM D1238
g/10 min
3
Molten Volume Flow Rate (MVR)
300°C/5.0 kg
ISO 1133
cm3/10min
1
Shrinkage rate - flow
-- 2
内部方法
%
0
Shrinkage rate - flow
3.20 mm
内部方法
%
0
Water absorption rate
饱和, 23°C
ISO 62
%
0
Water absorption rate
平衡, 23°C, 50% RH
ISO 62
%
0
Mechanical performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/V0150B-701
Tensile strength
屈服 4
ASTM D638
Mpa
7
Tensile strength
屈服
ISO 527-2/50
Mpa
7
Tensile strength
断裂 4
ASTM D638
Mpa
6
Tensile strength
断裂
ISO 527-2/50
Mpa
5
Tensile modulus
-- 3
ASTM D638
Mpa
2
Tensile modulus
--
ISO 527-2/1
Mpa
2
elongation
屈服 4
ASTM D638
%
5
elongation
屈服
ISO 527-2/50
%
4
elongation
断裂 4
ASTM D638
%
7
elongation
断裂
ISO 527-2/50
%
1
Taber abraser
1000 Cycles, 1000 g, CS-17 转轮
内部方法
mg
3
Bending modulus
50.0 mm 跨距 5
ASTM D790
Mpa
2
Bending modulus
-- 6
ISO 178
Mpa
2
Bending stress
-- 6, 7
ISO 178
Mpa
1
Bending stress
屈服, 50.0 mm 跨距 5
ASTM D790
Mpa
1
Thermal performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/V0150B-701
RTI
UL 746
°C
1
RTI Elec
UL 746
°C
1
RTI Imp
UL 746
°C
1
thermal conductivity
ISO 8302
W/m/K
0
Hot deformation temperature
0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 10
ISO 75-2/Be
°C
1
Hot deformation temperature
1.8 MPa, 未退火, 3.20 mm
ASTM D648
°C
1
Hot deformation temperature
1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 10
ISO 75-2/Ae
°C
1
Vicat softening temperature
--
ASTM D152511, ISO 306/B12011
°C
1
Vicat softening temperature
--
ISO 306/A50
°C
1
Vicat softening temperature
--
ISO 306/B50
°C
1
Linear coefficient of thermal expansion
流动 : -40 到 40°C
ASTM E831
cm/cm/°C
7
Linear coefficient of thermal expansion
流动 : 23 到 80°C
ISO 11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : -40 到 40°C
ASTM E831
cm/cm/°C
7
Linear coefficient of thermal expansion
横向 : 23 到 80°C
ISO 11359-2
cm/cm/°C
9
Electrical performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/V0150B-701
Surface resistivity
IEC 60093
ohms
>
Dielectric strength
0.800 mm, 在油中
IEC 60243-1
KV/mm
3
Dielectric strength
1.60 mm, 在油中
IEC 60243-1
KV/mm
2
Dielectric strength
3.20 mm, 在油中
IEC 60243-1
KV/mm
1
Leakage Trace Index
IEC 60112
V
2
Volume resistivity
IEC 60093
ohms·cm
1
Impact performance
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/V0150B-701
Impact strength of simply supported beam gap 8
-30°C
ISO 179/1eA
kJ/m²
5
Impact strength of simply supported beam gap 8
23°C
ISO 179/1eA
kJ/m²
1
Dart impact equipped with measuring instruments
23°C, Total Energy
ASTM D3763
J
5
hardness
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/V0150B-701
Ball pressure hardness
H 358/30
ISO 2039-1
Mpa
1
flammability
Test Condition
Test Method
Unit
PPO/SABIC INNOVATIVE SHANGHAI/V0150B-701
Extreme Oxygen Index
ISO 4589-2
%
3
Hot filament ignition temperature
1.0 mm
IEC 60695-2-13
°C
7
Hot filament ignition temperature
2.0 mm
IEC 60695-2-13
°C
7
Hot filament ignition temperature
3.0 mm
IEC 60695-2-13
°C
7
Burning wire flammability index
1.0 mm
IEC 60695-2-12
°C
9