Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | TD | ISO294-4 | 1.9 | % |
| Modeling Shrinkage | MD | ISO294-4 | 2.0 | % |
| Moisture Absorption | 23°C,24hr | ISO62 | 0.50 | % |
| Moisture Absorption | 饱和,23°C,2.00mm | ISO62 | 1.2 | % |
| Moisture Absorption | 平衡,23°C,2.00mm,50%RH | ISO62 | 0.20 | % |
| Melt Mass-Flow Rate | 190°C/2.16kg | ISO1133 | 15 | g/10min |
| Melt Volume flow Rate | 190°C/2.16kg | ISO1133 | 13.0 | cm3/10min |
| Density / Specific Gravity | | ISO1183 | 1.42 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Stress | | ISO178 | 77.0 | Mpa |
| Nominal Tensile Strain at Break | | ISO527-2 | 30 | % |
| Poisson Ratio | | ISO527 | 0.37 | |
| Tensile Stress | 屈服 | ISO527-2 | 70.0 | Mpa |
| Tensile Strain | 屈服 | ISO527-2 | 17 | % |
| Tensile Modulus | | ISO527-2 | 3100 | Mpa |
| Flexural Modulus | | ISO178 | 3000 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,未退火 | ISO75-2/B | 163 | °C |
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/A | 95.0 | °C |
| Vicat Softening Temperature | -- | ISO306/A50 | 174 | °C |
| Vicat Softening Temperature | -- | ISO306/B50 | 160 | °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 1.2E-04 | cm/cm/°C |
| Melting Temperature | | ISO11357-3 | 178 | °C |
| Annealing Temperature | | | 160 | °C |
| Annealing Time-Optional | | | 30.0 | min/mm |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Relative Permittivity | 100Hz | IEC60250 | 3.80 | |
| Relative Permittivity | 1MHz | IEC60250 | 3.80 | |
| Comparative Tracking Index | | IEC60112 | 600 | V |
| Dissipation Factor? | 100Hz | IEC60250 | 2.1E-03 | |
| Dissipation Factor? | 1MHz | IEC60250 | 5.6E-03 | |
| Surface Resistivity | | IEC60093 | 2E+13 | ohms |
| Volume Resistivity | | IEC60093 | >1.0E+15 | ohms·cm |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 260 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 260 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 8.0 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 9.0 | kJ/m² |
| Notched Izod Impact Strength | -40°C | ISO180/1A | 8.0 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 8.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | M计秤 | ISO2039-2 | 92 | |
| Rockwell Hardness | R计秤 | ISO2039-2 | 120 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| UL flame retardant rating | 0.8mm | IEC60695-11-10,-20 | HB | |
| FMVSS Flammability | | FMVSS302 | B | |
| atomization | F-value(refraction)4 | ISO6452 | 90 | % |
| atomization | G-value(condensate) | ISO6452 | 2E-04 | g |
| Burning Rate | 1.00mm | ISO3795 | 21 | mm/min |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| EmissionofOrganicCompounds | | VDA277 | 16.0 | µgC/g |
| Odor | | VDA270 | 6.00 | |
| Emission | | VDA275 | <8.00 | mg/kg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.