ASA/PC GELOY™ HRA222F-GY6G053 SABIC INNOVATIVE NANSHA
425
- Properties:High temperature resistanThermal stability
- Usages:Lawn garden equipmentHome appliance components
Compare
View PricesTechnical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.60 | % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.20 | % | |
| Outdoor Suitability | UL 746C | f1 | ||
| Melt Volume flow Rate | 260°C/2.16 kg | ISO 1133 | 13.0 | cm3/10min |
| Modeling Shrinkage - Flow | 内部方法 | 0.40 到 0.60 | % |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flexural Modulus | ISO 178 | 2510 | Mpa | |
| Flexural Stress | ISO 178 | 93.0 | Mpa | |
| Tensile Modulus | -- 3 | ASTM D638 | 2590 | Mpa |
| -- | ISO 527-2/1 | 2520 | Mpa | |
| Tensile Elongation | 屈服 5 | ASTM D638 | 4.2 | % |
| 屈服 4 | ASTM D638 | 4.3 | % | |
| 屈服 | ISO 527-2/5 | 4.3 | % | |
| 屈服 | ISO 527-2/50 | 4.4 | % | |
| 断裂 5 | ASTM D638 | > 100 | % | |
| 断裂 4 | ASTM D638 | > 100 | % | |
| 断裂 | ISO 527-2/5, ISO 527-2/50 | > 50 | % | |
| Tensile Strength | 屈服 4 | ASTM D638 | 63.0 | Mpa |
| 屈服 5 | ASTM D638 | 59.0 | Mpa | |
| 屈服 | ISO 527-2/5 | 62.0 | Mpa | |
| 屈服 | ISO 527-2/50 | 60.0 | Mpa | |
| 断裂 5 | ASTM D638 | 66.0 | Mpa | |
| 断裂 4 | ASTM D638 | 56.0 | Mpa | |
| 断裂 | ISO 527-2/5 | 51.0 | Mpa | |
| 断裂 | ISO 527-2/50 | 45.0 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | -- | ISO 306/A50 | 111 | °C |
| -- | ISO 306/B50 | 102 | °C | |
| -- | ISO 306/B120 | 104 | °C | |
| Ball PressureTest | 73 到 77°C | IEC 60695-10-2 | 通过 | |
| Linear thermal expansion coefficient | 流动 : -30 到 80°C | ISO 11359-2 | 6.9E-5 | cm/cm/°C |
| 横向 : -30 到 80°C | ISO 11359-2 | 7.1E-5 | cm/cm/°C | |
| 横向 : 23 到 80°C | ISO 11359-2 | 7.5E-5 | cm/cm/°C | |
| RTI | UL 746 | 90.0 | °C | |
| RTI Imp | UL 746 | 90.0 | °C | |
| RTI Elec | UL 746 | 90.0 | °C | |
| Heat Deflection Temperature | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Be | 99.0 | °C |
| 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 | ISO 75-2/Ae | 88.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Comparative Tracking Index | UL 746 | PLC 0 | ||
| IEC 60112 | 600 | V |
| Injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Drying Time | 2.0 到 4.0 | hr | ||
| Rear Temperature | 200 到 230 | °C | ||
| Middle Temperature | 220 到 260 | °C | ||
| Front Temperature | 230 到 270 | °C | ||
| Nozzle Temperature | 220 到 260 | °C | ||
| Drying Temperature | 80 到 90 | °C | ||
| Suggested Max Moisture | 0.020 | % | ||
| Processing (Melt) Temp | 230 到 270 | °C | ||
| Mold Temperature | 50 到 70 | °C | ||
| Hopper Temperature | 60 到 80 | °C |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Oxygen Index | ISO 4589-2 | 29 | % | |
| Flame Rating | 2.0 mm | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.