PC Makrolon® 9417 700394 COVESTRO SHANGHAI

262

Properties:
high viscosity
High temperature resistan
Filler: Glass fiber reinf
10% filler by weight
10% filler by weight
Usages:
Electronic and electrical
Automotive Applications
Certificates:
UL
Compare
View Prices

Technical Data Sheet

Physical Properties	Test Condition	Test Method	Test Result	Unit
Modeling Shrinkage	MD:2.00mm3	ISO294-4	0.60	%
	Modeling Shrinkage	TD	ISO2577	0.40to0.60	%
		Modeling Shrinkage	MD	ISO2577	0.40to0.60	%
		Modeling Shrinkage	Modeling Shrinkage	TD:2.00mm3	ISO294-4	0.45	%
Moisture Absorption	饱和,23°C	ISO62	0.26	%
Moisture Absorption	Moisture Absorption	平衡,23°C,50%RH	ISO62	0.10	%
Melt Mass-Flow Rate	300°C/1.2kg	ISO1133	7.0	g/10min
Melt Volume flow Rate	300°C/1.2kg	ISO1133	6.00	cm3/10min
Density / Specific Gravity	23°C	ISO1183	1.27	g/cm³
Apparent Density		ISO60	0.64	g/cm³

Mechanical Properties	Test Condition	Test Method	Test Result	Unit
Flexural Strain	23°C	ISO178	5.8	%
Flexural Stress	3.5%Strain,23°C	ISO178	95.0	Mpa
Flexural Stress	Flexural Stress	23°C	ISO178	105	Mpa
Flexural Modulus	23°C	ISO178	3600	Mpa
Tensile Creep Modulus	1hr	ISO899-1	3600	Mpa
Tensile Stress	屈服,23°C	ISO527-2/5	64.0	Mpa
Tensile Stress	Tensile Stress	断裂,23°C	ISO527-2/5	45.0	Mpa
Tensile Strain	屈服,23°C	ISO527-2/5	4.6	%
Tensile Strain	Tensile Strain	断裂,23°C	ISO527-2/5	15	%
Tensile Creep Modulus	1000hr	ISO899-1	2900	Mpa
Tensile Modulus	23°C	ISO527-2/1	3800	Mpa

Thermal Properties	Test Condition	Test Method	Test Result	Unit
Deflection Temperature Under Load?	0.45MPa,未退火	ISO75-2/B	141	°C
Deflection Temperature Under Load?	Deflection Temperature Under Load?	1.8MPa,未退火	ISO75-2/A	135	°C
Ball PressureTest	136°C	IEC60695-10-2	Pass
RTIElec	1.5mm	UL746	125	°C
Evolution Calendar intelligent importer	1.5mm	UL746	115	°C
RTIStr	1.5mm	UL746	125	°C
Vicat Softening Temperature	--	ISO306/B50	143	°C
Vicat Softening Temperature	Vicat Softening Temperature	--	ISO306/B120	144	°C
Linear thermal expansion coefficient	MD：23到55°C	ISO11359-2	4E-05	cm/cm/°C
Linear thermal expansion coefficient	Linear thermal expansion coefficient	TD：23to55°C	ISO11359-2	6.5E-05	cm/cm/°C
Thermal Conductivity	23°C	ISO8302	0.22	W/m/K

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dielectric Strength	23°C,1.00mm	IEC60243-1	36	KV/mm
Dissipation Factor?	23°C,100Hz	IEC60250	1E-03
Dissipation Factor?	Dissipation Factor?	23°C,1MHz	IEC60250	9E-03
Relative Permittivity	23°C,100Hz	IEC60250	3.20
Relative Permittivity	Relative Permittivity	23°C,1MHz	IEC60250	3.20
Comparative Tracking Index	解决方案A	IEC60112	175	V
Comparative Tracking Index	Comparative Tracking Index	解决方案B	IEC60112	125	V
Surface Resistivity		IEC60093	1E+16	ohms
Volume Resistivity	23°C	IEC60093	1E+16	ohms·cm

Impact Properties	Test Condition	Test Method	Test Result	Unit
Charpy Unnotched Impact Strength	-60°C,CompleteBreak	ISO179/1eU	100	kJ/m²
	Charpy Unnotched Impact Strength	-30°C,完全断裂	ISO179/1eU	120	kJ/m²
	Charpy Unnotched Impact Strength	Charpy Unnotched Impact Strength	23°C,完全断裂	ISO179/1eU	150	kJ/m²
Multi-Axial Instrumented Impact Energy	23°C	ISO6603-2	25.0	J
Multi-Axial Instrumented Impact Energy	Multi-Axial Instrumented Impact Energy	-30°C	ISO6603-2	15.0	J
	23°C,CompleteBreak	ISO7391	10	kJ/m²
Notched Izod Impact Strength	23°C,CompleteBreak	ISO7391	10	kJ/m²
Multi-Axial Instrumented Impact Peak Force	-30°C	ISO6603-2	3700	N
Multi-Axial Instrumented Impact Peak Force	Multi-Axial Instrumented Impact Peak Force	23°C	ISO6603-2	4000	N

hardness	Test Condition	Test Method	Test Result	Unit
Ball Indentation Hardness		ISO2039-1	128	Mpa

Flammability	Test Condition	Test Method	Test Result	Unit
Oxygen Index		ISO4589-2	35	%
ApplicationofFlamefromSmallBurner MethodKandF	2.00mm	DIN53438-1,-3	K1,F1
UL flame retardant rating	1.5mm	UL94	V-0
	UL flame retardant rating	3.0mm,NC,BK,GY	UL94	5VA
	UL flame retardant rating	UL flame retardant rating	6.0mm	UL94	5VA
Glow Wire Flammability Index	0.75mm	IEC60695-2-12	960	°C
	Glow Wire Flammability Index	1.5mm	IEC60695-2-12	960	°C
	Glow Wire Flammability Index	Glow Wire Flammability Index	3.0mm	IEC60695-2-12	960	°C
Glow Wire Ignition Temperature	1.0mm	IEC60695-2-13	825	°C
	Glow Wire Ignition Temperature	1.5mm	IEC60695-2-13	900	°C
	Glow Wire Ignition Temperature	Glow Wire Ignition Temperature	3.0mm	IEC60695-2-13	900	°C
FMVSS Flammability	>1.00mm	ISO3795	passed
FlashIgnition		ASTMD1929	470	°C
SelfIgnition		ASTMD1929	550	°C

Supplementary information	Test Condition	Test Method	Test Result	Unit
ElectrolyticalCorrosion	23°C	IEC60426	A1
ISO Shortname			ISO7391-PC,MFLR,(,,)-09-9,GF10

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.