ASA KIBILAC® PW-957 TAIWAN CHIMEI
473
- Properties:High glossHigh mobilityWeather resistance
- Usages:Electrical toolsElectrical fieldElectrical appliancesElectronic fieldAutomotive sectorLighting fixtures
- Certificates:MSDSRoHSULTDSTDSULMSDSRoHSSVHCProcessing物质宣告书
Compare
View PricesTechnical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density | ASTM D792/ISO 1183 | 1.07 | ||
| Melt Mass-Flow Rate | ASTM D1238/ISO 1133 | 28 | g/10min |
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Modeling Shrinkage | ISO294-4 | 0.40to0.70 | % | |
| Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 23 | g/10min |
| Melt Volume flow Rate | 220°C/10.0kg | ISO1133 | 23.0 | cm3/10min |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile Strength | 屈服 | ASTMD638 | 43.0 | Mpa |
| Flexural Modulus | ASTMD790 | 2160 | Mpa | |
| Flexural Strength | ASTMD790 | 63.3 | Mpa | |
| Tensile strength | ASTM D-638 | 420 | kg/cm | |
| Tensile Elongation | 断裂 | ASTMD638 | 55 | % |
| Flexural Modulus | ISO178 | 2200 | Mpa | |
| Flexural Stress | ISO178 | 67.0 | Mpa | |
| Tensile Stress | 屈服 | ISO527-2/50 | 46.0 | Mpa |
| 断裂 | ISO527-2/50 | 33.0 | Mpa | |
| Tensile Strain | 断裂 | ISO527-2/50 | 20 | % |
| Tensile Strength | ASTM D638/ISO 527 | 440 | kg/cm²(MPa)[Lb/in²] | |
| Flexural Strength | ASTM D790/ISO 178 | 650 | kg/cm²(MPa)[Lb/in²] | |
| ASTM D-790 | 550 | kg/cm | ||
| Izod Impact Strength | 1/8" | ASTM D-256 | 15 | kg.cm/cm |
| Izod notch impact strength | ASTM D256/ISO 179 | 10 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 15 | kg·cm/cm(J/M)ft·lb/in |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat Softening Temperature | ASTM D-1525 | 105 | °C | |
| ASTMD15256 | 105 | °C | ||
| -- | ISO306/A50 | 105 | °C | |
| -- | ISO306/B50 | 94.0 | °C | |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 9E-05 | cm/cm/°C |
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/A | 80.0 | °C |
| 1.8MPa,退火 | ISO75-2/A | 97.0 | °C | |
| Annealed | ASTMD648 | 95 | °C | |
| Unannealed | ASTMD648 | 85 | °C | |
| ASTM D648/ISO 75 | 95 | ℃（℉） | ||
| ASTM D648/ISO 75 | 85 | ℃（℉） | ||
| Vicat Softening Temperature | ASTM D1525/ISO R306 | 105 | ℃（℉） |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell Hardness | R级 | ASTMD785 | 105 |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
| Physical | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 220℃,10kg | ASTM D-1238 | 28 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.