Technical Data Sheet
| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Moisture Absorption | 饱和,23°C,2.00mm | ISO62 | 6.3 | % |
| Moisture Absorption | 平衡,23°C,2.00mm,50%RH | ISO62 | 1.9 | % |
| Modeling Shrinkage | TD | ISO294-4 | 0.60 | % |
| Modeling Shrinkage | MD | ISO294-4 | 0.20 | % |
| MediumDensity | | | 1.20 | g/cm³ |
| SpecificHeatCapacityofMelt | | | 2280 | J/kg/°C |
| ThermalConductivityofMelt | | | 0.26 | W/m/K |
| Melt Volume flow Rate | 250°C/5.0kg | ISO1133 | 15.0 | cm3/10min |
| Density / Specific Gravity | | ISO1183 | 1.36 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Modulus | | ISO178 | 8500 | Mpa |
| Flexural Stress | | ISO178 | 280 | Mpa |
| Tensile Creep Modulus | 1hr | ISO899-1 | -- | Mpa |
| Tensile Creep Modulus | 1000hr | ISO899-1 | -- | Mpa |
| Tensile Stress | 断裂 | ISO527-2 | 190 | Mpa |
| Tensile Strain | 断裂 | ISO527-2 | 3.5 | % |
| Tensile Modulus | | ISO527-2 | 9500 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 0.45MPa,未退火 | ISO75-2/B | 220 | °C |
| Deflection Temperature Under Load? | 1.8MPa,未退火 | ISO75-2/A | 210 | °C |
| Vicat Softening Temperature | | ISO306/B50 | 215 | °C |
| Linear thermal expansion coefficient | MD | ISO11359-2 | 2.6E-05 | cm/cm/°C |
| Linear thermal expansion coefficient | TD | ISO11359-2 | 7.5E-05 | cm/cm/°C |
| Effective Thermal Diffusivity | | | 9.1E-08 | m²/s |
| Melting Temperature | | ISO11357-3 | 221 | °C |
| Glass Transition Temperature | | ISO11357-2 | 60.0 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Multi-Axial Instrumented Impact Energy | 23°C | ISO6603-2 | 3.50 | J |
| Notched Izod impact strength | 23°C | ISO180/1U | 80 | kJ/m² |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 16 | kJ/m² |
| Notched Izod Impact Strength | -30°C | ISO180/1A | 10 | kJ/m² |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 15 | kJ/m² |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 80 | kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 100 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R级 | ISO2039-2 | 121 | |
| Ball Indentation Hardness | H961/30 | ISO2039-1 | 230 | Mpa |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| UL flame retardant rating | 1.5mm | UL94 | HB | |
| UL flame retardant rating | 0.75mm | IEC60695-11-10,-20 | HB | |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | HB | |
| FMVSS Flammability | | FMVSS302 | B | |
| Burning Rate | 1.00mm | ISO3795 | 50 | mm/min |
| Oxygen Index | | ISO4589-2 | 21 | % |
| atomization | F-value(refraction) | ISO6452 | 95 | % |
| atomization | G-value(condensate) | ISO6452 | 1E-04 | g |
| Supplementary information | Test Condition | Test Method | Test Result | Unit |
|---|
| EmissionofOrganicCompounds | | VDA277 | 8.50 | µgC/g |
| Odor | | VDA270 | 3.50 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.