| Physical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Modeling Shrinkage | MD：3.20mm | ASTMD955 | 0.40to0.70 | % |
| Modeling Shrinkage | MD：3.20mm | ISO294-4 | 0.40to0.70 | % |
| Melt Mass-Flow Rate | 220°C/10.0kg | ASTMD1238 | 6.0 | g/10min |
| Melt Mass-Flow Rate | 220°C/10.0kg | ISO1133 | 6.0 | g/10min |
| Density / Specific Gravity | | ASTMD792 | 1.08 | g/cm³ |
| Density / Specific Gravity | | ISO1183 | 1.08 | g/cm³ |
| Mechanical Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Flexural Modulus | | ISO178 | 2400 | Mpa |
| Flexural Strength | 6.40mm | ASTMD790 | 75.5 | Mpa |
| Flexural Modulus | 6.40mm | ASTMD790 | 2300 | Mpa |
| Tensile Strength | 屈服,3.20mm | ASTMD638 | 47.1 | Mpa |
| Tensile Elongation | 断裂,3.20mm | ASTMD638 | 20 | % |
| Flexural Stress | | ISO178 | 75.0 | Mpa |
| Tensile Stress | 屈服 | ISO527-2/50 | 48.0 | Mpa |
| Tensile Modulus | | ISO527-2/1 | 2200 | Mpa |
| Thermal Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Deflection Temperature Under Load? | 1.8MPa,未退火,6.40mm | ASTMD648 | 94.0 | °C |
| Vicat Softening Temperature | | ASTMD15256 | 102 | °C |
| Vicat Softening Temperature | | ISO306/B50 | 102 | °C |
| RTIElec | | UL746 | 50.0 | °C |
| Evolution Calendar intelligent importer | | UL746 | 50.0 | °C |
| Heat Deflection Temperature | 1.8MPa,Unannealed,4.00mm | ISO75-2/Ae | 88.0 | °C |
| Impact Properties | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 11 | kJ/m² |
| Notched Izod Impact Strength | 23°C,6.40mm | ASTMD256 | 140 | J/m |
| Notched Izod Impact Strength | 23°C | ISO180/1A | 12 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell Hardness | R级 | ASTMD785 | 104 | |
| Rockwell Hardness | | ISO2039-2 | 104 | |
| Flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.